钢制筒形容器薄壁板立缝焊接防变形方法技术
Anti deformation method for vertical seam welding of thin wall plate of steel cylinder container
A steel cylindrical vessel wall board vertical welding deformation preventing method, comprising the following steps: 1. Vessel wall adjust positioning welding interface after welding butt weld; the vessel wall and curved plate respectively in upper and lower arc plate in the vessel wall and wall on both sides of the butt weld welding firmly; in the butt weld on both sides in the vessel wall and lateral welding deformation preventing channel. The invention has the effect of restricting the welding shrinkage deformation through the function of the anti deformation channel reinforcing rib, and is favorable for controlling the wave deformation (concave) phenomenon of the vertical seam welding of the thin-wall container plate. At the same time, it is conducive to ensuring product quality, reducing the workload of the late rectification, reducing construction costs.
【技术实现步骤摘要】
钢制筒形容器薄壁板立缝焊接防变形方法
：本专利技术属于钢结构工程焊接
，尤其涉及一种钢制筒形容器薄壁板立缝焊接防变形方法。
技术介绍
：目前大量油、水等液体储存容器选用了钢制筒形容器，此类容器由于压力较小,上部壁板所用钢板设计一般较薄，在焊接时变形较大。通常壁板立缝焊接时在焊缝上、中、下分别焊接防变形弧板来实现壁板接口组装定位和防止焊接变形，此种方法虽能防止一定的角变形，但由于壁板焊接时受纵向和横向收缩应力的影响，薄壁板在未加弧板处易产生波浪变形(向内凹陷)。
技术实现思路
本专利技术的目的是提供一种钢制筒形容器薄壁板立缝焊接防变形方法，该方法有效地解决了目前常见的薄壁筒形容器立缝焊接内凹变形的问题并且操作方便。如上构思，本专利技术的技术方案是：一种钢制筒形容器薄壁板立缝焊接防变形方法，其特征在于：包括如下步骤：①将容器壁板调整好对接口后进行定位焊，焊接对接焊缝；②在容器壁板上、下分别加弧形板，弧形板在容器壁板对接焊缝两侧部分与壁板焊接牢固；③在对接焊缝两侧分别在容器壁板内外侧加焊防变形槽钢。上述弧形板采用钢板制作，厚度大于容器壁板厚度，弧度与容器壁板外壁弧度一...
【技术保护点】
一种钢制筒形容器薄壁板立缝焊接防变形方法，其特征在于：包括如下步骤：①将容器壁板调整好对接口后进行定位焊，焊接对接焊缝；②在容器壁板上、下分别加弧形板，弧形板在容器壁板对接焊缝两侧部分与壁板焊接牢固；③在对接焊缝两侧分别在容器壁板内外侧加焊防变形槽钢。
【技术特征摘要】
1.一种钢制筒形容器薄壁板立缝焊接防变形方法，其特征在于：包括如下步骤：①将容器壁板调整好对接口后进行定位焊，焊接对接焊缝；②在容器壁板上、下分别加弧形板，弧形板在容器壁板对接焊缝两侧部分与壁板焊接牢固；③在对接焊缝两侧分别在容器壁板内外侧加焊防变形槽钢。2.根据权利要求1所述的钢制筒形容器薄壁板立缝焊接防变形方法，其特征在于：上述弧形板采用钢板制作，厚度大于...
【专利技术属性】
技术研发人员：杨志刚，王玢，王金林，韩晓强，杨俊刚，
申请(专利权)人：中冶天工集团有限公司，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。