The invention discloses a solar tin plating process, the process comprises the following steps: Step 1, ultrasonic cleaning with butt welding, cleaning solution in dilute hydrochloric acid solution, ethanol, deionized water after drying, standby; step 2, embossed groove in welding with the imprint technology; step 3, tin the molten coating coated on the groove, an inert environment can be dry. Compared with the prior art, the invention of a solar photovoltaic welding with tin plating process, the preparation of welding with coating thickness is easy to control, reduce the amount of tin, the welding strip surface uniform, good conductivity, and the preparation process and low requirements for equipment for mass production.
【技术实现步骤摘要】
一种太阳能光伏焊带镀锡工艺
本专利技术属于太阳能光伏
，具体涉及一种太阳能光伏焊带镀锡工艺。
技术介绍
焊带是焊接太阳能光伏组件的常用焊接材料，传统的焊带采用热浸镀工艺，即焊带基材铜带经过烧熔的锡炉，锡料附着在基材表面，冷凝后形成锡层。虽然镀层很明显，但是用锡量大，镀层表面不均一，厚度在20-25微米，导电性一般，极容易产生锡渣、锡缝等。申请号200910181579.5的中国专利公开了一种超软态光伏焊带的制造方法，并具体公开了制备方法包括以下步骤：1、将无氧铜丝精轧并经连续管式退火；2、用清水对退火后的无氧铜丝进行超声波清洗；3、清洗后的铜带用助焊剂浸湿，并浸入锡炉涂锡；4、唉锡鲁出口处安装一个自动化调速引风机，涂锡铜带从锡炉出来后首先经过引风机，然后经自动引用机和自动收线机上盘即成焊带成品。本专利的焊带可焊性强、伸长率高、碎片率低，但是该主带涂层厚度不一，比较废锡液，成本比较高。申请号201110100009.6的中国专利公开了一种太阳能光伏焊带着色工艺，具体公开的步骤如下：1、将铜质焊带用于与太阳能光伏电池连接的一面浸入熔融状态的锡金属中，使焊带与太阳...
【技术保护点】
一种太阳能光伏焊带镀锡工艺，其特征在于，包括以下步骤：步骤1，对焊带超声清洗，清洗液依次为稀盐酸溶液、乙醇、去离子水后烘干，备用；步骤2，采用压印技术在焊带上压印出凹槽；步骤3，将熔融的锡液采用刮涂方式涂在凹槽内，惰性环境下晾干，即可。
【技术特征摘要】
1.一种太阳能光伏焊带镀锡工艺，其特征在于，包括以下步骤：步骤1，对焊带超声清洗，清洗液依次为稀盐酸溶液、乙醇、去离子水后烘干，备用；步骤2，采用压印技术在焊带上压印出凹槽；步骤3，将熔融的锡液采用刮涂方式涂在凹槽内，惰性环境下晾干，即可。2.根据权利要求1所述的一种太阳能光伏焊带镀锡工艺，其特征在于，步骤1中稀盐酸溶液的质量份数为1-3%。3.根据权利要求1所述的一种太...
【专利技术属性】
技术研发人员：庄益春，卞祖慧，贾敏，陈宁，
申请(专利权)人：江苏东昇光伏科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。