本发明专利技术涉及一种颚式破碎机的耐磨衬板，它由以下重量百分比的组分组成：10~25%粘结相，75~90%硬质相，所述粘结相为CoCrTiAlMoY合金，所述硬质相由WC和TiAlSi组成，所述WC占所述颚式破碎机的耐磨衬板的重量百分比为30~50%，所述TiAlSi占所述颚式破碎机的耐磨衬板颚式破碎机的耐磨衬板的重量百分比为25~60％。这样能够提高粘结相在高温时的延展性而使其均匀覆在硬质相的表面，使得制得的合金工具具有高强度、硬度和韧性，抗氧化温度达到1600℃以上，并且有很好的耐磁性。

Wear resistant lining plate for jaw crusher

The invention relates to a jaw crusher wear-resistant liner, it consists of the following components in weight percentage: 10~25% bonding phase, 75~90% hard phase, the bonding phase of CoCrTiAlMoY alloy, the hard phase by WC and TiAlSi WC, the weight percentage of the jaw crusher wear the lining board is 30~50%, the TiAlSi weight percentage of the jaw crusher jaw crusher liner wear abrasion resistant lining board for 25~60%. This can improve the bonding phase ductility at high temperature and the uniform coating of hard phase in the surface of the prepared alloy tool has the advantages of high strength, hardness and toughness, oxidation temperature more than 1600 DEG C, and has good resistance to magnetic.

【技术实现步骤摘要】
一种颚式破碎机的耐磨衬板
本专利技术属于金属合金制造领域，具体涉及一种颚式破碎机的耐磨衬板。
技术介绍
矿山机械是直接用于矿物开采和富选等作业的机械，包括采矿机械和选矿机械。探矿机械的工作原理和结构与开采同类矿物所用的采矿机械大多相同或相似，广义上说，探矿机械也属于矿山机械。另外，矿山作业中还应用大量的起重机、输送机、通风机和排水机械等。旋转钻机用于露天矿山岩石硬度系数f≤6的岩层钻孔，同时也可钻f＝7-11的硬夹层岩石。钻进时施加回转力矩与轴压力，使钻头作旋转与进给运动，来切割岩石。产品变型后可改变孔径、孔深或改装凿岩台车或潜孔钻。颚式破碎机是旋转导向钻井技术中非常重要的部件，其质量的优劣直接影响钻机在十分复杂恶劣的施工过程能否完成设定的工作任务，其结构的设计和硬度是完成上述工作任务的关键性能。传统硬质合金是以Co、Co、Fe单质元素为粘结相、以WC为硬质相。随着使用温度的升高，特别是在400℃以上，Co、Co、Fe单质元素为粘结相和WC硬质相开始发生氧化，WC氧化生成WO3，Co氧化生成CoWO4，氧化物疏松多孔，不具有保护性，导致传统硬质合金抗弯强度、硬度等性能显著降低，高温使本文档来自技高网...

【技术保护点】
一种颚式破碎机的耐磨衬板，它由以下重量百分比的组分组成：10~25%粘结相，75~90%硬质相，其特征在于：所述粘结相为CoCrTiAlMoY合金，所述硬质相由WC和TiAlSi组成，所述WC占所述颚式破碎机的耐磨衬板的重量百分比为30~50%，所述TiAlSi占所述颚式破碎机的耐磨衬板颚式破碎机的耐磨衬板的重量百分比为25~60%。

【技术特征摘要】
1.一种颚式破碎机的耐磨衬板，它由以下重量百分比的组分组成：10~25%粘结相，75~90%硬质相，其特征在于：所述粘结相为CoCrTiAlMoY合金，所述硬质相由WC和TiAlSi组成，所述WC占所述颚式破碎机的耐磨衬板的重量百分比为30~50%，所述TiAlSi...