The invention discloses a load type defluoridators, including sand, and sand deposited on the surface of the inorganic fluoride removal agent, the inorganic fluoride removing sand agent and the mass ratio of 4:1 1:1. The invention relates to a load type fluorine removing agent suitable for industrial fixed bed, with yellow sand as a load carrier, stable performance, high adsorption capacity, fluoride removal efficiency is high; the invention of a load type defluoridators can be reused many times, in situ regeneration, regeneration still has good adsorption effect; a load the present invention defluoridators broad source of raw materials, easy, low price; supported the preparation equipment and process simple fluorine agent of the invention, mild reaction conditions, suitable for industrial mass production.
【技术实现步骤摘要】
一种负载型除氟剂及其制备方法
本专利技术涉及除氟材料
，具体地是涉及一种负载型除氟剂及其制备方法。
技术介绍
我国高氟地下水分布广泛，遍布27个省、市级自治区，尤其华北、西北地区最为严重。长期饮用氟超标的水，可能导致氟斑牙、氟骨病、老年痴呆等病症。世界卫生组织建议饮用水中氟化物的浓度不超过1.5mg/L，我国现行的饮用水标准规定氟化物不超过1.0mg/L，因此，人们开发了多种去除水中氟化物的方法。目前，主要的除氟方法包括沉淀法、电化学法、膜分离法、离子交换法、吸附法。吸附法兼具操作简单、效果稳定、经济可行等优点被广泛采用，但此方法的核心在于高效吸附剂的开发。常用的氧化铝除氟剂，吸附量低，难以达到令人满意的效果。专利CN103285804A公开了一种镍镁铝除氟剂，主要利用双滴共沉淀法合成镍镁铝三元水滑石材料，再经过煅烧得到具有较大表面积的材料，此种除氟剂对于氟离子的吸附量惊人，但这种粉末材料，在实际应用中存在一个严重问题，即用于固定床时压降太大，机械强度差，活性组分流失严重，而且焙烧态的材料回收利用较困难，导致难以工业化应用。专利CN100593433C公开了...
【技术保护点】
一种负载型除氟剂，其特征在于：包括黄沙，以及沉积在所述黄沙表面的无机除氟剂，所述无机除氟剂和所述黄沙的质量比为4:1‑1:1。
【技术特征摘要】
1.一种负载型除氟剂，其特征在于：包括黄沙，以及沉积在所述黄沙表面的无机除氟剂，所述无机除氟剂和所述黄沙的质量比为4:1-1:1。2.如权利要求1所述的一种负载型除氟剂，其特征在于：所述无机除氟剂具有层状晶体结构。3.一种如权利要求1或2任一所述的负载型除氟剂的制备方法，其特征在于包括以下步骤：步骤1)溶液配制：配制0.4mol/L-1.5mol/L的盐水溶液，配制2mol/L-3mol/L的氢氧化钠水溶液或氢氧化钠和碳酸钠混合物的水溶液；所述盐水溶液为镁盐、镍盐、铝盐或铁盐的水溶液中的一种或多种；步骤2)黄沙预处理：将原料黄沙过60-80目筛，取筛下黄沙经去离子水清洗、烘干；步骤3)反应：在步骤2)得到的黄沙中加入去离子水...
【专利技术属性】
技术研发人员：蔡建国，石洪雁，付晓微，
申请(专利权)人：江苏海普功能材料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。