The invention relates to a corundum spinel castable and preparation method thereof, belonging to the field of inorganic non-metallic materials. The solution is: to the quality fraction of 60~70% particles, 10~18% tabular corundum tabular corundum powder, 5~9% fused spinel and 8~12% activated alumina powder, 0~8% MgO NiO TiO2 clinker powder as raw material, and adding the quality of raw materials for 1~3% with water reducing agent and cement 0.2~0.6% after the raw material; pre mixing, adding water mixing, 3~5% casting, prepared corundum spinel castable. The invention has the advantages of compact structure of the pouring material, high temperature strength, good thermal shock resistance and corrosion resistance, can be widely used for the package, the package bottom wall of ladle, brick and air core and other parts, and prolong its service life.
【技术实现步骤摘要】
一种刚玉-尖晶石浇注料及其制备方法
本专利技术属于不定型耐火浇注料领域。具体涉及一种刚玉-尖晶石浇注料及其制备方法。
技术介绍
刚玉-尖晶石浇注料作为新一代高级耐火材料，因其优异的高温强度、抗渣侵蚀和渗透性，已在精炼钢包、电炉、中间包等设备上得到广泛应用，主要用作大型钢包衬、钢包透气砖等。近年来由于钢铁工业连铸及二次精练工艺的快速发展，对于刚玉尖晶石浇注料的使用条件也越来越苛刻，随着炼钢温度的提高和钢水在钢包中停留时间的延长，钢包工作面在1600℃以上的环境下受到了高温渣的侵蚀与渗透，大大降低了其使用寿命。传统工艺的刚玉尖晶石浇注料已无法满足技术进步的需求，恶劣的使用环境亟需通过提高刚玉-尖晶石浇注料各方面性能来应对。向刚玉-尖晶石浇注料中引入一些氧化物，来改善浇注料的性能，已经有很多人进行了探索。经检索：申请号为201210229504.1的专利申请公开了一种引入氧化铬的刚玉-浇注料，虽然已经有所提高浇注料的抗渣能力，但还不能满足现有钢厂的生产要求；根据崔庆阳等人的研究表明，随着ZrO2的引入含量的不断增加，渗透层的厚度先变小后增大[崔庆阳，毛晓刚，吴林林，王辉...
【技术保护点】
一种刚玉‑尖晶石浇注料，其特征在于：按质量分数比，原料组成为：60~70%的板状刚玉颗粒、10~18%的板状刚玉细粉、5~9%的电熔镁铝尖晶石、8~12%的活性氧化铝微粉、0~8%的MgO‑NiO‑TiO2熟料细粉为原料，并加入原料质量为1~3%的铝酸盐水泥结合剂以及0.2~0.6%的减水剂。
【技术特征摘要】
1.一种刚玉-尖晶石浇注料，其特征在于：按质量分数比，原料组成为：60~70%的板状刚玉颗粒、10~18%的板状刚玉细粉、5~9%的电熔镁铝尖晶石、8~12%的活性氧化铝微粉、0~8%的MgO-NiO-TiO2熟料细粉为原料，并加入原料质量为1~3%的铝酸盐水泥结合剂以及0.2~0.6%的减水剂。2.根据权利要求1所述的刚玉-尖晶石浇注料，其...
【专利技术属性】
技术研发人员：涂军波，连伟康，王义龙，张连进，马伟平，李金雨，唐冰杰，魏军从，