The present invention relates to RH refining furnace bottom with magnesium chrome ramming material and its production method, the magnesium chrome ramming material composed of Cr20 sand, South Africa chrome, MgO more than 96.5% high purity magnesia chrome ore, chrome ore, Oman Brazil, after mixing and adding binder. The binding agent is composed of anhydrous Magnesium Sulfate, citric acid, boric acid, sodium citrate and six sodium hexametaphosphate. The invention adopts a variety of raw materials containing chromium and high purity magnesia mixing magnesite chrome ramming material made by bonding agent, has good corrosion resistance, long service life, can completely replace the imported products with the domestic refractories for metallurgical furnace, reduces production cost.
【技术实现步骤摘要】
一种RH精炼炉炉底用镁铬质捣打料及其生产方法
本专利技术涉及耐火材料
，尤其涉及一种RH精炼炉炉底用镁铬质捣打料及其生产方法。
技术介绍
镁铬质耐火材料是一种含三氧化二铬的镁质耐火材料，氧化铬通过固熔于方镁石和形成低膨胀的镁铬尖晶石，可增大液相对耐火相的润湿角，提高直接结合程度，生成理想的方镁石-镁铬尖晶石-微裂纹复合结构，使镁铬质耐火材料具有良好的荷重软化温度、高温强度、抗侵蚀性、热震稳定性、较低的导热率和较好的挂窑皮性。目前我国RH精炼炉炉底用的镁铬质耐火材料普遍依靠进口，其成本高，增加了企业生产运行负担。
技术实现思路
本专利技术提供了一种RH精炼炉炉底用镁铬质捣打料及其生产方法，采用多种含铬原料与高纯镁砂通过结合剂混练制成镁铬质捣打料，具有耐侵蚀性好，使用寿命长的优点，完全可以取代国外进口产品实现冶金电炉用耐火材料的国产化，降低了企业生产成本。为了达到上述目的，本专利技术采用以下技术方案实现：一种RH精炼炉炉底用镁铬质捣打料，其特征在于，所述镁铬质捣打料由以下原料按重量份比例制成：Cr20砂：3＜粒度≤5mm，1～20份；1＜粒度≤3mm，1～15份；0...
【技术保护点】
一种RH精炼炉炉底用镁铬质捣打料，其特征在于，所述镁铬质捣打料由以下原料按重量份比例制成：Cr20砂：3＜粒度≤5mm，1～20份；1＜粒度≤3mm，1～15份；0＜粒度≤1mm，1～15份；南非铬矿：200目，5～10份；MgO≥96.5％高纯镁砂：1＜粒度≤3mm，5～10份；0＜粒度≤1mm，1～10份；200目，10～20份；阿曼铬矿：3＜粒度≤5mm，5～10份；巴西铬矿：1＜粒度≤3mm，1～20份；0＜粒度≤1mm，1～15份；200目，1～10份；结合剂：5～23份。
【技术特征摘要】
1.一种RH精炼炉炉底用镁铬质捣打料，其特征在于，所述镁铬质捣打料由以下原料按重量份比例制成：Cr20砂：3＜粒度≤5mm，1～20份；1＜粒度≤3mm，1～15份；0＜粒度≤1mm，1～15份；南非铬矿：200目，5～10份；MgO≥96.5％高纯镁砂：1＜粒度≤3mm，5～10份；0＜粒度≤1mm，1～10份；200目，10～20份；阿曼铬矿：3＜粒度≤5mm，5～10份；巴西铬矿：1＜粒度≤3mm，1～20份；0＜粒度≤1mm，1～15份；200目，1～10份；结合剂：5～23份。2.根据权利要求1所述的一种RH精炼炉炉底用镁铬质捣打料，其特征在于，所述结合剂按重量份比例由以下组分组成：无水硫酸镁1～5份，柠檬酸1...
【专利技术属性】
技术研发人员：金钊，张义先，董会彬，陈东明，尹斌，王健骁，
申请(专利权)人：海城市中兴镁质合成材料有限公司，海城市中兴高档镁质砖有限公司，
类型：发明
国别省市：辽宁,21