The present invention provides a method, a Cu Pd alloy catalyst for high concentration of glycerol producing lactic acid comprises the following steps: using biomass glycerol as raw materials, the reaction temperature is 180 to 240 DEG C, the reaction time is 1 ~ 2H under anaerobic conditions and alkaline environment, adding Cu Pd alloy catalyst, lactic acid was obtained in anaerobic reaction autoclave. The method of the invention has low reaction temperature, high conversion rate, glycerol selectivity, high reaction rate and catalyst reuse advantages of high performance, simple process safety and environmental protection, has good prospects for industrialization.
【技术实现步骤摘要】
本专利技术涉及乳酸制备
，特指一种双金属Cu-Pd合金催化剂催化转化高浓度甘油制备乳酸的方法。
技术介绍
乳酸(lacticacid)是三大有机酸之一，是一种重要的生物化工产品，主要应用在食品和医药等工业；由于乳酸对人体无副作用，容易吸收，可直接参与体内代谢，促进消化及抑制肠道内的有害细菌等作用，故应用十分广泛。乳酸及其衍生物被公认为是安全的食品添加剂；乳酸在医药工业中，由于乳酸具有很强的杀菌作用，强极性和亲水性，同时它又可作为收敛性杀菌剂，还能降低血清胆固醇，增强人体免疫力。另外，乳酸聚合得到聚乳酸，聚乳酸可以抽成丝纺成线；乳酸在皮革工业、化妆品工业、卷烟生产等行业中都有着广泛的用途，乳酸可以合成聚乳酸，聚乳酸作为生物降解性塑料，可广泛应用于制造一次性食品包装袋、食品容器、包装纸、购物袋、卫生用纸、农用薄膜等，有利于保护生态环境，防止环境污染，因此，乳酸的需求量将越来越大。传统乳酸生产采用糖为原料的发酵技术，甘油浓度10％，生物酶为催化剂。存在产量低，生物废水多，成本高的问题。甘油作为生产生物柴油的副产品，期产量非常庞大，约占生物柴油总体的10％～20％...
【技术保护点】
一种Cu‑Pd合金催化剂催化高浓度甘油制备乳酸的方法，其特征在于，步骤如下：以生物质甘油为原料，反应温度为180～240℃，反应时间为1～2h，在无氧条件以及碱性环境下，加入Cu‑Pd合金催化剂，在无氧高压反应釜中进行反应得到乳酸。
【技术特征摘要】
1.一种Cu-Pd合金催化剂催化高浓度甘油制备乳酸的方法，其特征在于，步骤如下：以生物质甘油为原料，反应温度为180～240℃，反应时间为1～2h，在无氧条件以及碱性环境下，加入Cu-Pd合金催化剂，在无氧高压反应釜中进行反应得到乳酸。2.根据权利要求1所述的一种Cu-Pd合金催化剂催化高浓度甘油制备乳酸的方法，其特征在于，所述Cu-Pd合金催化剂中，铜钯摩尔比为100:2～5。3.根据权利要求1所述的一种Cu-Pd合金催化剂催化高浓度甘油制备乳酸的方法，其特征在于，所述甘油以水溶液形式存在，其浓度为3～6mol/L。4.根据权利要求1所述的一种Cu-Pd合金催化剂催化高浓度甘油制备乳酸的方法，其特征在于，所述Cu-Pd合金催化剂可重复利用，可重复利用次数不低于8次。5.根据权利要求1所述的一种Cu-Pd合金催化剂催化高浓度甘油制备乳酸的方法，其特征在于，所述的Cu-Pd合金催化剂的添加量与甘油质量比为0.02～0.05:1。6.根据权利要求1所述的一种Cu-Pd...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。