一种KNb3O8纳米棒的制备方法技术
Method for preparing KNb3O8 nanorods
The invention discloses a method for preparing KNb3O8 nanorods, the invention will be a certain amount of niobium oxalate, oxalate and potassium acetate dissolved in a volume of two N, N dimethylformamide, and then slowly adding PVP (K 90, polyvinylpyrrolidone), mixing precursor liquid cream color; the milky white precursor liquid electrostatic spinning in a certain voltage, flow rate and relative humidity of atmosphere; and then the electrostatic spinning products sintered KNb3O8 nanorods. Electrochemical experiments show that the KNb3O8 nanorods prepared by this method have broad application prospects as anode materials for lithium ion batteries. In the preparation process, the operation is simple, the raw material cost is low, the equipment investment is low, and the utility model is suitable for mass production.
【技术实现步骤摘要】
一种KNb3O8纳米棒的制备方法
本专利技术属于材料化学领域，具体涉及到一种KNb3O8纳米棒的制备方法。
技术介绍
相对于大块材料而言，纳米材料因自身结构的特殊性，在很多方面具有更为优异的性能，除此之外，纳米材料还有很多大块材料没有的新性能。这些特性导致其在很多方面具有广泛潜在应用。在所有维度的纳米材料中，一维纳米材料有在两个维度都受限的特殊结构，导致其产生了很多新的物理化学特性，所以其具有非常多的其它维度的纳米材料没有的性能或者较它们来说更为优异的性能。在铌酸钾类化合物中，KNbO3应用最为广泛。KNbO3、K4Nb6O17，K2Nb4O11，K2Nb8O21主要应用于压电陶瓷、光波导器件、激光倍频器、声表面波传感器、光通讯、光催化等领域。LongtuLi等人用静电纺丝技术制备KNbO3纳米纤维，并研究了其光催化性能(RSCAdvances,2015,5,72410-72415)。2001年，YuhaoLu首次将KNb5O13作为电极材料应用于锂离子电池中，并探讨了KNb5O13在充放电过程中可能的嵌锂机制(YuhaoLu等人，Chem.Mater.,2011...
【技术保护点】
一种KNb3O8纳米棒的制备方法，其特征在于，所述KNb3O8纳米棒的制备方法包括以下步骤：1)称取一定量草酸铌，草酸和乙酸钾溶于一定体积的N,N‑二甲基甲酰胺中，然后缓慢加入适量的聚乙烯吡咯烷酮，搅拌6‑18h，得到乳白色的前驱体液；2)将得到的乳白色的前驱体液在20～30kv电压和0.6～1.0mL/h流率下、相对湿度为30～50％的氛围下进行静电纺丝；3)将得到的静电纺丝产品置于坩埚内，然后将坩埚放置于马弗炉中700～800℃烧结3～5h，然后自然降温至室温，得到KNb3O8纳米棒。
【技术特征摘要】
1.一种KNb3O8纳米棒的制备方法，其特征在于，所述KNb3O8纳米棒的制备方法包括以下步骤：1)称取一定量草酸铌，草酸和乙酸钾溶于一定体积的N,N-二甲基甲酰胺中，然后缓慢加入适量的聚乙烯吡咯烷酮，搅拌6-18h，得到乳白色的前驱体液；2)将得到的乳白色的前驱体液在20～30kv电压和0.6～1.0mL/h流率下、相对湿度为30～50％的氛围下进行静电纺丝；3)将得到的静电纺丝产品置于坩埚内，然后将坩埚放置于马弗炉中700～800℃烧结3～5h，然后自然降温至室温，得到K...