一种类钙钛矿层状结构化合物及其制备方法技术
A kind of calcium titanium ore layer structure compound and preparation method thereof
The present invention provides a kind of calcium titanium ore layer structure compound and a preparation method thereof. The invention provides a kind of layered perovskite structure compounds with molecular formula Bi7Fe2Ti2O17Cl, molecular design and previous to the perovskite layer of magnetic ions doped different modulation, the invention of bismuth oxide modulation, makes bismuth oxide layer and the perovskite structure was formed by the new unit, the class of layered perovskite structure compounds with good ferroelectric properties, magnetic glass behavior showed a weak ferromagnetic and magnetoelectric coupling properties, has a good potential application in information storage and other functional materials.
【技术实现步骤摘要】
一种类钙钛矿层状结构化合物及其制备方法
本法明涉及无机材料
，特别涉及一种类钙钛矿层状结构化合物及其制备方法。
技术介绍
类钙钛矿层状结构的化合物最早由科学家B.Aurivillius发现，因此又被称为Aurivillius化合物，其是一种典型的无公度的长周期结构的化合物，结构通式为(Bi2O2)(An-1BnO3n+1)，其中n大于等于1，A表示离子半径较大的12配位阳离子，B表示离子半径较小的6配位阳离子，表现为类钙钛矿层(An-1BnO3n+1)与铋氧层(Bi2O2)沿着各自晶胞参数的c方向周期性交替堆垛。目前，这一类材料在电容器、非易失铁电随机存取存储器、压电器件、多铁材料等信息能源领域有着广泛的应用。该类化合物中这种长程有序的堆垛结构具有一定的结构容忍性，为材料的分子设计及功能设计提供了很好的母体结构。例如，利用铁电材料钛酸铋(Bi4Ti3O12)对一些钙钛矿层的容忍性，可以将磁性层BiFeO3嵌入到钙钛矿层中，形成结构式为(Bi2O2)(Bin-1Ti3Fen-3O3n+1)的材料；目前，针对这一体系的研究，主要集中于钙钛矿层磁性离子的掺杂以及周...
【技术保护点】
一种类钙钛矿层状结构化合物，其特征在于，具有式(1)所示分子式：Bi7Fe2Ti2O17Cl 式(1)。
【技术特征摘要】
1.一种类钙钛矿层状结构化合物，其特征在于，具有式(1)所示分子式：Bi7Fe2Ti2O17Cl式(1)。2.一种类钙钛矿层状结构化合物的制备方法，其特征在于，包括以下步骤：a)将铋源化合物、钛源化合物、铁源化合物和氯源化合物混合，得到混合粉体；b)将所述混合粉体预烧，得到预烧粉体；c)将所述预烧粉体烧结，得到具有式(1)所示分子式的类钙钛矿层状结构化合物；Bi7Fe2Ti2O17Cl式(1)。3.根据权利要求2所述的制备方法，其特征在于，所述铋源化合物选自氧化铋或硝酸铋；所述钛源化合物为二氧化钛；所述铁源化合物选自三氧化二铁或硝酸铁；所述氯源化合物为氧氯化铋。4.根据权利要求2所述的制备方法，其特征在于，所述步骤b)中，所述预烧的温度为700～800℃，所述预烧的时间为2～5h。5.根据权利要求2或4所述的制备方法，其特征在于，所述步骤b)中，所述预烧的升温速率为3～8℃/min。6.根据权利要求2所述...
【专利技术属性】
技术研发人员：陆亚林，陈泽志，彭冉冉，王建林，傅正平，唐浩文，
申请(专利权)人：中国科学技术大学，
类型：发明
国别省市：安徽,34