The invention discloses a method for preparing silicon carbide powder, bamboo charcoal powder as the carbon source, using TEOS as silicon source, which comprises the following steps: (1) with the diameter of 0.35 ~ 0.8 m bamboo charcoal powder; (2) preparation of bamboo charcoal powder dispersion: bamboo charcoal powder, glucose mixture acid and deionized water, with strong mechanical stirring for 1 to 2 hours; (3) the TEOS added to the step (2) in the preparation of bamboo charcoal powder dispersion liquid, stirring for 3 to 5 hours, filtering and washing with anhydrous ethanol and dried, then solid in a vacuum high temperature sintering furnace after drying in 1500 ~ 1800 DEG C under heating 3 ~ 5 hours, get SiC powder. The carbon source and the silicon source of the invention form a mixed reaction system with ultra close contact, and the silicon carbide micropowder prepared by the invention has high purity and uniform particle size distribution.
【技术实现步骤摘要】
一种碳化硅微粉的制备方法
本专利技术涉及一种碳化硅微粉的制备方法，具体是以竹炭微粉为碳源，正硅酸乙酯为硅源制备碳化硅微粉的方法。
技术介绍
作为一种新型的精细陶瓷，碳化硅材料以其优异的物理化学性能而日益受到重视，其中碳化硅粉体特性是影响碳化硅陶瓷材料性能的主要因素。碳热反应是一种合成碳化硅粉体的主要方法之一，目前规模化碳热反应生产碳化硅粉体的是Acheson法，但该方法存在杂质含量多、粒径不易控制等缺点，在一定程度上限制了碳化硅材料的应用。高纯度、粒径可控是碳热合成碳化硅粉末发展的主要方向，其关键是选择合适的硅源、碳源以及工艺条件。长期以来，硅源多采用石英砂、二氧化硅粉体、硅粉、硅烷等，近年来，含有高反应活性的二氧化硅纳米粒子的硅溶胶被认为是合成碳化硅的最有效的硅源之一。碳源的选择局限于石墨、碳粉，一些含碳高分子如蔗糖、淀粉、酚醛树脂、沥青等也有广泛研究。石墨和碳粉作为碳源，与硅粉等生成碳化硅主要为固相反应，而固相反应过程存在接触面积有限、反应不充分等缺点，影响了碳化硅粉体的收得率；而以高分子为碳源虽然可以获得一定纯度、晶型及粒度可控的碳化硅粉末，但反应复杂、产率...
【技术保护点】
一种碳化硅微粉的制备方法，其特征在于：以竹炭微粉为碳源，以正硅酸乙酯为硅源，以重量份计，包括以下步骤：(1)选用粒径在0.35～0.8μm的竹炭微粉；(2)制备竹炭微粉分散液：将10～12份竹炭微粉、0.5～2份葡萄糖酸和65～80份去离子水混合，经强力机械搅拌1～2小时；(3)，将42～210份正硅酸乙酯加入到步骤(2)中制备的竹炭微粉分散液中，搅拌反应3～5小时，过滤用无水乙醇洗涤，并干燥，然后将干燥后的固体置于真空高温烧结炉中，在1500～1800℃下加热3～5小时，得到碳化硅微粉。
【技术特征摘要】
1.一种碳化硅微粉的制备方法，其特征在于：以竹炭微粉为碳源，以正硅酸乙酯为硅源，以重量份计，包括以下步骤：(1)选用粒径在0.35～0.8μm的竹炭微粉；(2)制备竹炭微粉分散液：将10～12份竹炭微粉、0.5～2份葡萄糖酸和65～80份去离子水混合，经强力机械搅拌1～2小时；(3)，将42～210份正硅酸乙酯加入到步骤(...
【专利技术属性】
技术研发人员：时松超，张瑞芳，关春旺，
申请(专利权)人：郑州西利康新材料有限公司，
类型：发明