The invention of aramid fiber / Kenaf hybrid siro spinning Phil aramid filament composite yarn and its processing method based on composite yarn is composed of two aramid filaments and an aramid fiber hybrid kenaf drafting after strand twisting, two aramid filament and aramid fiber hybrid kenaf roving after drafting to be a spiral in the composite yarn surface alternately arranged orderly. The spinning draft of an aramid fiber hybrid kenaf roving and spinning machine front roller feeding back two aramid filament pull, twisting in front converging front roller to form a composite yarn; two sides of two aramid filaments in front roller end are respectively located in the aramid fiber kenaf hybrid, two aramid filament spacing is 6 ~ 12mm. The present invention solves for kenaf fiber caused by rough yarn hairiness and yarn strength more kenaf / aramid fiber blended lead to the problem of low, has the characteristics of high strength, less hairiness, low price, can be widely used in protective textiles.
【技术实现步骤摘要】
本专利技术属于纺纱领域，特别是涉及一种基于赛络菲尔纺的洋麻芳纶混合纤维/芳纶长丝复合纱线及其加工方法。
技术介绍
本申请人在申请号CN201310041191.1的专利技术专利申请《一种洋麻与芳纶混纺纱线的制造方法》中，公开了一种将洋麻依次经柔软处理、纤维剪短和喷洒梳理剂并密封处理，将芳纶短纤经喷洒梳理剂并密封处理，然后把两者混合，并依次经开松、梳理、并条、粗纱和细纱工序加工成为洋麻与芳纶混纺纱线的制造方法。上述制造方法由于主要采用现有棉纺工艺设备，为适应毛纺梳理工序（梳理工序采用毛纺罗拉梳理机）的工艺条件，因此需要对所述两种纤维施以短切工艺，即柔软处理后的洋麻纤维和芳纶纤维的长度均为45～50mm。上述混纺纱线的洋麻纤维和芳纶纤维的重量百分比分别为30～35%和70～65%。上述制造方法的显著效果是开拓性地提供了洋麻纤维与芳纶纤维混纺纱线新品种，该混纺纱线可以减少芳纶产品中芳纶纤维的用量而降低芳纶产品的成本，并且明显地改善了芳纶产品抗静电性能差的缺陷，为芳纶产品广泛应用提供了有利条件。但是，上述制造方法获...
【技术保护点】
基于赛络菲尔纺的洋麻芳纶混合纤维/芳纶长丝复合纱线，其特征在于：由两根芳纶长丝和一根洋麻芳纶混合纤维粗纱牵伸后的须条加捻结合构成，所述两根芳纶长丝与洋麻芳纶混合纤维粗纱牵伸后的须条螺旋状有序交替排布于复合纱线表面。
【技术特征摘要】
1.基于赛络菲尔纺的洋麻芳纶混合纤维/芳纶长丝复合纱线，其
特征在于：由两根芳纶长丝和一根洋麻芳纶混合纤维粗纱牵伸后的须
条加捻结合构成，所述两根芳纶长丝与洋麻芳纶混合纤维粗纱牵伸后
的须条螺旋状有序交替排布于复合纱线表面。
2.基于赛络菲尔纺的洋麻芳纶混合纤维/芳纶长丝复合纱线的加
工方法，其特征在于包括：经细纱机牵伸的一根洋麻芳纶混合纤维粗
纱须条与细纱机前罗拉后端喂入的两根芳纶长丝在前罗拉前端汇合，
经加捻形成复合纱线；所述两根芳纶长丝在前罗拉后端分别位于洋麻
芳纶混合纤维须条的两侧，两根芳纶长丝间距为6～12mm。
3.根据权利要求2所述的加工方法，其特征...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。