The invention discloses a PVC/ strip winding pipe, which is composed of the following parts by weight of the raw material is prepared by polyvinyl chloride 100, 0 to 10 portions of polyvinyl chloride and thermoplastic polyester elastomer 0 - 10, 0 - 5, graphene Ca / Zn stabilizer 0.1 - 1, OP wax 0.1 ~ 1. The invention provides a PVC/ steel strip winding pipe, high ring stiffness, can well meet the design requirements of municipal drainage, sewage irrigation, hydropower, mine ventilation, the use of seawater pipeline ring stiffness; in addition, the invention of the PVC/ steel pipe, also has less material, cost low, easy corrosion, long service life, compared with the existing pipe products, save material cost more than 30%, 25% lower than that of the very significant economic benefits, so it is worthy of popularization and application.
【技术实现步骤摘要】
一种PVC/钢带缠绕管及其制备方法与应用
本专利技术涉及一种PVC/钢带缠绕管及其制备方法与应用
技术介绍
PVC缠绕管是现在生产、生活中常用的一种管材，然而目前PVC缠绕管的环刚度较低，难以实现市政排水排污、农业灌溉、水力发电、矿井通风、海水养殖等领域大于8KN/m2的环刚度设计要求。同时，现有的PVC缠绕管，缠绕难度大，在实际生产中存在不易操作、物耗高、成本高等缺陷，不利于企业提高生产效率和经济效益。为了解决上述问题，克服现有的缺陷，需要开发一种新的PVC缠绕管。
技术实现思路
本专利技术的目的在于提供一种环刚度高的PVC/钢带缠绕管。为达到上述目的，本专利技术采用的技术方案如下：一种PVC/钢带缠绕管，它是由以下重量份数的原料制备而成：聚氯乙烯100份、氯化聚氯乙烯0～10份、热塑性聚酯弹性体0～10份、石墨烯0～5份、钙/锌稳定剂0.1～1份、OP蜡0.1～1份。进一步的，它是由以下重量份数的原料制备而成：聚氯乙烯100份、氯化聚氯乙烯3～8份、热塑性聚酯弹性体3～5份、石墨烯0.5～0.8份、钙/锌稳定剂0.1～1份、OP蜡0.1～1份。进一步的，它是由以下...
【技术保护点】
一种PVC/钢带缠绕管，其特征在于：它是由以下重量份数的原料制备而成：聚氯乙烯100份、氯化聚氯乙烯0～10份、热塑性聚酯弹性体0～10份、石墨烯0～5份、钙/锌稳定剂0.1～1份、OP蜡0.1～1份。
【技术特征摘要】
1.一种PVC/钢带缠绕管，其特征在于：它是由以下重量份数的原料制备而成：聚氯乙烯100份、氯化聚氯乙烯0～10份、热塑性聚酯弹性体0～10份、石墨烯0～5份、钙/锌稳定剂0.1～1份、OP蜡0.1～1份。2.根据权利要求1所述的PVC/钢带缠绕管，其特征在于：它是由以下重量份数的原料制备而成：聚氯乙烯100份、氯化聚氯乙烯3～8份、热塑性聚酯弹性体3～5份、石墨烯0.5～0.8份、钙/锌稳定剂0.1～1份、OP蜡0.1～1份。3.根据权利要求2所述的PVC/钢带缠绕管，其特征在于：它是由以下重量份数的原料制备而成：聚氯乙烯100份、氯化聚氯乙烯3份、热塑性聚酯弹性体3份、石墨烯0.5份、钙/锌稳定剂0.5份、OP蜡0.3份。4.根据权利要求1～3任意一项所述的PVC/钢带缠绕管，其特征在于：所述氯化聚氯乙烯的氯含量62～66％。5.根据权利要求1～3任意一项所述的PVC/钢带缠绕管，其特征在于：所述热塑性聚酯弹性体的硬度...
【专利技术属性】
技术研发人员：邱承勋，
申请(专利权)人：淄博海能塑管有限公司，
类型：发明
国别省市：山东,37