高强度PVC复合材料制造技术

本发明专利技术公开了一种高强度PVC复合材料，由塑料、蒙脱土粒子、碳酸钙粒子和各种助剂组成，各组分的重量配比为：塑料60～70％，蒙脱土粒子5～6％，碳酸钙粒子5～6％，相容剂8～11％，润滑剂7～8％，增韧剂2～4％；进一步改进在于：蒙脱土粒子、碳酸钙粒子采用硅烷进行处理，润滑剂为硬脂酸或液体石蜡。本发明专利技术加入蒙脱土粒子、碳酸钙粒子，提高本发明专利技术拉伸、抗冲击性能，制造费用低。

High strength PVC composite

The invention discloses a high strength PVC composite material, composed of plastic, montmorillonite particles, particles of calcium carbonate and various additives, the components by weight percent: Plastic 60 ~ 70%, 5 ~ 6% montmorillonite particles, calcium carbonate particles of 5 ~ 6%, 8 ~ 11% compatibilizer, lubricant 7 ~ 8%. Toughening agent 2 ~ 4%; further improvement that montmorillonite particles, calcium carbonate particles were treated by silane and stearic acid as lubricant or liquid paraffin. The invention adds montmorillonite particles and calcium carbonate particles, and improves the tensile and impact resistance property of the invention, and the manufacture cost is low.

【技术实现步骤摘要】
高强度PVC复合材料
本专利技术涉及一种高分子复合材料，特别是一种PVC复合材料。
技术介绍
随着纳米技术的发展，采用纳米技术提高PVC复合材料性能已得到应用，但已得到应用的纳米粒子种类较少，限制了纳米技术在PVC复合材料方面的应用。
技术实现思路
本专利技术针对现有技术的不足，提出一种能增加纳米粒子在PVC复合材料应用上种类的高强度PVC复合材料。本专利技术通过下述技术方案实现技术目标。高强度PVC复合材料，其改进之处在于：由塑料、蒙脱土粒子、碳酸钙粒子和各种助剂组成，各组分的重量配比为：塑料60～70％，蒙脱土粒子5～6％，碳酸钙粒子5～6％，相容剂8～11％，润滑剂7～8％，增韧剂2～4％。进一步改进在于：所述蒙脱土粒子、碳酸钙粒子采用硅烷进行处理。进一步改进在于：所述润滑剂为硬脂酸或液体石蜡。本专利技术与现有技术相比，具有以下积极效果：1、加入蒙脱土粒子、碳酸钙粒子，提高本专利技术拉伸、抗冲击性能；另一方面，碳酸钙粒子价格较低，显著降低了本专利技术的制造费用。2、采用蒙脱土粒子、碳酸钙粒子，增加纳米粒子在PVC复合材料应用上种类。3、蒙脱土粒子、碳酸钙粒子采用硅烷进行处理，进一步本文档来自技高网...

【技术保护点】
一种高强度PVC复合材料，其特征在于：由塑料、蒙脱土粒子、碳酸钙粒子和各种助剂组成，各组分的重量配比为：塑料60～70％，蒙脱土粒子5～6％，碳酸钙粒子5～6％，相容剂8～11％，润滑剂7～8％，增韧剂2～4％。

【技术特征摘要】
1.一种高强度PVC复合材料，其特征在于：由塑料、蒙脱土粒子、碳酸钙粒子和各种助剂组成，各组分的重量配比为：塑料60～70％，蒙脱土粒子5～6％，碳酸钙粒子5～6％，相容剂8～11％，润滑剂7～8％，增...

【专利技术属性】
技术研发人员：郭新，
申请(专利权)人：郭新，
类型：发明
国别省市：江苏,32