偏光片、显示装置及偏光片的制备方法制造方法及图纸

本发明专利技术公开一种偏光片、显示装置及偏光片的制备方法，所述偏光片包括偏光膜，所述偏光膜为吸附有二色性材料的纤维素纳米纤维膜。由于纤维素纳米纤维具有良好的成膜性，光透过性高，热膨胀系数小，使用吸附有二色性材料的纤维素纳米纤维膜作为偏光膜，可以有效解决现有技术中的偏光片由于温度和湿度变化引起的偏光膜的收缩翘曲导致漏光的问题。

Polarizing plate, display device and method for preparing polarizing plate

The invention discloses a polarizing plate, a display device and a preparation method of polarizing plate, wherein the polarizing plate comprises a polarizing film which is a cellulose nanofiber membrane adsorbing two color material. Because of the cellulose fiber has good film-forming properties, high light transmittance, low thermal expansion coefficient, adsorption cellulose nano fiber membrane material as two color polarizing film, polarizing film can effectively solve the existing technology in the polarizing film caused by the variation of temperature and humidity of the shrinkage and warpage caused the problem of light leakage.

【技术实现步骤摘要】
偏光片、显示装置及偏光片的制备方法
本专利技术涉及显示器
，特别是涉及一种偏光片、显示装置及偏光片的制备方法。
技术介绍
偏光片是液晶显示屏的基础部品之一，是一种只允许特定方向偏振光穿透的薄膜面板，在液晶面板的制作过程中，上下各贴1片偏光片，且偏振方向需要呈垂直方向，主要作用是在电场变化作用于液晶时，使光源产生相位差而呈现明暗状态，用以显示字体和图案等。目前偏光片中最常用的偏光膜为高分子二色性型，一般常用PVA(聚乙烯醇)材料，吸附上二色性材料(碘系、染料系等)，使碘离子或染料均匀吸附在PVA分子表面，加热后再单向延伸PVA膜，达到吸收二色性的功能。拉伸前PVA分子为任意角度无规则分布，受力拉伸后分子逐渐朝向拉伸方向，吸附在PVA分子上的碘分子也随之产生方向性，因此可以吸收平行于它排布方向的偏振光，只允许垂直方向的偏振光通过。液晶面板因为使用时温度湿度的变化，会导致配置在液晶面板两侧的偏光片发生收缩，参照图1，为现有技术中偏光片收缩示意图。偏光片的收缩主要是因为偏光膜中拉伸的PVA分子在热的作用下由有序回归无序状态引起。液晶面板因为偏光膜的收缩而发生翘曲，会导致漏光现象。现有技本文档来自技高网...

【技术保护点】
一种偏光片，其特征在于，包括：偏光膜，所述偏光膜为吸附有二色性材料的纤维素纳米纤维膜。

【技术特征摘要】
1.一种偏光片，其特征在于，包括：偏光膜，所述偏光膜为吸附有二色性材料的纤维素纳米纤维膜。2.根据权利要求1所述的偏光片，其特征在于，所述偏光膜一侧依次层叠设置有第一保护层、压敏胶层和离型膜；和所述偏光膜另一侧依次层叠设置有第二保护层和保护膜。3.根据权利要求2所述的偏光片，其特征在于，所述第一保护层和所述第二保护层均为三醋酸纤维素层，厚度均为10un～20um。4.根据权利要求2所述的偏光片，其特征在于，所述压敏胶层的厚度为5um。5.根据权利要求1-4任一项所述的偏光片，其特征在于，所述纤维素纳米纤维膜的厚度为5～10um。6.一种显示面板，其特征在于，包括如权利要求1-5任一项所述的偏光片。7.一种偏光片的制...

【专利技术属性】
技术研发人员：彭晓青，王凯旋，袁洪亮，马力，陈会顺，
申请(专利权)人：京东方科技集团股份有限公司，北京京东方光电科技有限公司，
类型：发明