一种干熄焦料钟用耐火耐磨扇形板制造技术

本发明专利技术公开了一种干熄焦料钟用耐火耐磨扇形板，包括耐火耐磨扇形板体，板体底部为弧形，板体顶部具有卡口，所述卡口为板体上内陷形成的折角。本发明专利技术采用氮化硅耐火砖材质设计成拼接式的料钟底部，避免了传统技术中铸钢材料加耐磨焊条组合，整体形态稳定，而且耐磨性远远优于铸钢材料。

Refractory wear-resistant fan-shaped plate for quenching coke bell

The invention discloses a fire-resistant and abrasion resistant fan-shaped plate for a quenching coke bell, which comprises a refractory and wear-resistant fan-shaped plate body; the bottom of the plate body is arc-shaped; the top of the plate body is provided with a bayonet; the bayonet is a folding angle formed on the plate body. The invention adopts the silicon nitride refractory brick material to be designed as a splicing type material bell bottom, and avoids the combination of the cast steel material and the wear-resisting welding rod in the traditional technology, and the overall shape is stable, and the abrasion resistance is much better than that of the cast steel material.

【技术实现步骤摘要】
一种干熄焦料钟用耐火耐磨扇形板
本专利技术属于耐火材料领域，具体涉及一种干熄焦料钟用耐火耐磨扇形板。
技术介绍
自2000年实施干熄焦引进技术吸收开发项目以来，我国干熄焦技术得到了迅速发展，到目前为止，我国已投产和在建的干熄焦装置达到了200余座，干熄焦国产化技术和设备得到全面开发和应用，且实现了干熄焦装置的系列化和大型化。近年来，国家对节能减排的政策要求越来越高，焦炉的大型化，高效化，清洁环保生产和自动化方面要求逐渐提高，与焦炉相匹配的干熄焦装置随即跟进，最主要的是其处理能力的扩大，随之而来的技术难点就有：如何让红焦粒度分布均匀并均匀沉降，从而改善干熄焦炉内红焦冷却的性能。混用装入装置的固定式钟型布料器（以下简称料钟），对红焦装入过程中在干熄炉内圆周方向及半径方向的均匀分布起着决定性的作用，其设计复杂，现一般均用铸钢加耐磨焊条堆焊，这种材料在红焦的多次冲击下，耐磨性差、容易损坏、寿命短，影响正常生产。
技术实现思路
专利技术目的：本专利技术的目的在于针对现有技术的不足，提供一种干熄焦料钟用耐火耐磨扇形板。技术方案：为了达到上述专利技术目的，本专利技术具体是这样来完成的：一种干熄焦料钟用本文档来自技高网...

【技术保护点】
一种干熄焦料钟用耐火耐磨扇形板，包括耐火耐磨扇形板体（1），板体（1）底部为弧形，其特征在于，板体（1）顶部具有卡口（2），所述卡口（2）为板体（1）上内陷形成的折角。