一种基于乳铁蛋白活性的新型生物材料的制备方法技术
Preparation method of novel biological material based on lactoferrin activity
The invention discloses a method for preparing a novel biological material based on the activity of lactoferrin, will have osteogenic activity of lactoferrin as a new bone growth factor in bone tissue engineering, to solve the various bone growth factors are difficult to obtain, the problem of expensive. Can be loaded on the hydroxyapatite / collagen implant materials, the interaction between lactoferrin and hydroxyapatite / collagen composite materials, the lactoferrin release slowly, to solve the problem of the short half-life of load growth factor. To some extent, the bone viability of hydroxyapatite / collagen implants was improved, and the biological activity of single biomaterials was low.
【技术实现步骤摘要】
一种基于乳铁蛋白活性的新型生物材料的制备方法
本专利技术涉及一种生物材料，具体是一种基于乳铁蛋白活性的新型生物材料的制备方法。
技术介绍
随着现代社会人口老龄化问题的加剧，骨创伤、骨肿瘤以及其它骨骼疾病的发病率居高不下，直接导致了大量的骨折和骨缺损患者。据统计，我国每年骨缺损患者超过500万人，其中因骨质疏松引起的脊柱和四肢骨骼等的骨折患者人数在200万人以上，因骨肿瘤切除、人工关节周围骨溶解、脊柱融合等需进行骨移植手术的患者约40万例，而这些患者大多面临着植骨治疗。目前，传统植骨治疗手段主要包括自体骨移植和异体骨移植。自体骨移植一直称为行业的“金标准”，但其来源有限，供体骨形状和结构不合适，又会对患者造成二次创伤，使用受到一定限制。而异体骨移植也存在免疫排斥反应以及携带疾病的可能，直接影响植骨治疗的效果。因此研究开发生物相容性好生物性能接近自体骨组织，无免疫排斥反应的人造骨组织一直是再生医学领域研究和探索的热点。而随着医学工程的发展，骨组织工程的出现逐渐引起了广泛的关注。其主要原理是将种子细胞种植于复合了细胞因子的支架材料上，形成三维复合体，植入骨缺损部位，在生...
【技术保护点】
一种基于乳铁蛋白活性的新型生物材料的制备方法，其特征在于，步骤如下：将HAP/Col粉末加入乳铁蛋白溶液中，HAP/Col粉末的加入量为乳铁蛋白质量的的0.2%～1%，30～40℃反应5～30h，过滤离心，取上清液，并用超纯水对复合物粉末冲洗去除杂质，然后冷冻干燥的方式对得到的HAP/Col‑LF复合材料进行干燥处理。
【技术特征摘要】
1.一种基于乳铁蛋白活性的新型生物材料的制备方法，其特征在于，步骤如下：将HAP/Col粉末加入乳铁蛋白溶液中，HAP/Col粉末的加入量为乳铁蛋白质量的的0.2%～1%，30～40℃反应5～30h，过滤离心，取上清液，并用超纯水对复合物粉末冲洗去除杂质，然后冷冻干燥的方式对得到的HAP/Col-LF复合材料进行干燥处理。2.根据权利要求1所述的基于乳铁蛋白活性的新型生物材料的制备方法，其特征在于，羟基磷灰石/胶原粉末的制备方法：取80～120mL胶原蛋白溶液，逐滴加入1～2mol/L的Ca(NO3)2搅拌10～30min后滴加0.5～1mol/L的(NH4)2HPO4溶液，控制反应温度10℃以下，继续搅拌30～90min，以0.5～1mol/L氢氧化钠滴定溶液pH至6～8，同时收集白色沉淀，蒸馏水反复洗涤沉淀，冻干后制得羟基磷灰石/胶原粉末。...
【专利技术属性】
技术研发人员：杜明，石璞洁，于翠平，刘猛，樊凤娇，吴迪，
申请(专利权)人：大连工业大学，
类型：发明
国别省市：辽宁,21