The invention relates to a magnetic fiber cloth, belonging to the technical field of functional fiber cloth. The technical problem solved by the invention is to provide a magnetic fiber cloth with good comfortability. The invention of magnetic fabric, consists of the following components by weight percent: woven magnetic fiber from 20 to 30%; 15 to 20% silk viscose fiber; 5 ~ 10%; PTFE fiber 2 ~ 8% and 2 ~ 8%; alginate fiber; polyester fiber for the rest. The invention adopts the specific method to prepare the magnetic fiber, the magnetic particles are evenly embedded in the fiber, not easy to fall off, resistant to washing and friction, high fiber strength and good magnetism. The magnetic fiber cloth prepared by the magnetic fiber has the advantages of light weight, soft texture, good air permeability, high comfort and good magnetic treatment function.
【技术实现步骤摘要】
磁性纤维布
本专利技术涉及磁性纤维布，属于功能纤维布
技术介绍
人类发现磁铁已有3500年的历史，人们对磁疗在很早以前就开始进行了应用。例如：15世纪，瑞士医生Paracelsus证明了磁铁的医疗保健作用，他在国际上发表了首篇关于磁铁对抗机体炎症的医学研究论文。又例如：16世纪，英国医生WilliamGiibert开展了大量的电与磁的研究，并出版了世界上最早的磁疗著作“DeMagne”。磁性纤维是一种对人体具有一定保健作用的功能纤维。人体具有生物磁场，每一个细胞都是一个微磁单元，因此外界磁场的变化会通过神经、体液等系统影响人体的生理机能。基于这种原理，将具有磁性的纺织纤维织造成保健织物——如塑身保健内衣等，来调整人体的机能，可以起到抗病保健的效果。磁性纤维一般采用混纺的方法制得，磁粉的含量将会极大程度的影响纤维的强度，如果磁粉含量高，其强度将会降低，因此，为保证纤维的强度，共混纺丝法生产的磁性纤维的磁粉用量在15％以下，这样大大限制了磁性纤维的磁性。此外，采用磁性纤维制备的产品，一般是制成直接接触皮肤的贴身衣服使用，如内衣、内裤、护膝、护肘等，但是现有的...
【技术保护点】
磁性纤维布，其特征在于，由以下重量百分比的组分纺织而成：磁性纤维20～30％；粘胶纤维15～20％；蚕丝5～10％；聚四氟乙烯纤维2～8％；海藻纤维2～8％；其余为涤纶纤维。
【技术特征摘要】
1.磁性纤维布，其特征在于，由以下重量百分比的组分纺织而成：磁性纤维20～30％；粘胶纤维15～20％；蚕丝5～10％；聚四氟乙烯纤维2～8％；海藻纤维2～8％；其余为涤纶纤维。2.根据权利要求1所述的磁性纤维布，其特征在于，由以下重量百分比的组分纺织而成：磁性纤维22～28％；粘胶纤维16～18％；蚕丝5～10％；聚四氟乙烯纤维3～5％；海藻纤维3～6％；其余为涤纶纤维。3.根据权利要求2所述的磁性纤维布，其特征在于，由以下重量百分比的组分纺织而成：磁性纤维26％；粘胶纤维17％；蚕丝7％；聚四氟乙烯纤维4...
【专利技术属性】
技术研发人员：张科，
申请(专利权)人：成都磁动势科技有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。