The invention discloses a preparation method of nylon yarn Eugen, the method of attapulgite, graphene and antibacterial plant extracts added in nylon slices, the addition of graphene and attapulgite can increase the stiffness of fiber and fixation properties; adding antibacterial plant extracts can increase the antibacterial fiber the effect of anti ultraviolet properties; fiber also has certain enhancement; and nanometer calcium carbonate spray on the surface of nylon fiber, nylon fiber surface modification, anti ultraviolet properties of nylon fiber will be further enhanced, the invention made of nylon yarn not only has Eugen, crisp, good UV resistant and solid the color properties, and good antibacterial properties.
【技术实现步骤摘要】
一种锦纶欧根纱的制备方法
本专利技术涉及面料的制备方法，属于纺织
，尤其涉及一种锦纶欧根纱的制备方法。
技术介绍
欧亘纱，也叫柯根纱，也有叫欧根纱，欧跟纱。英文名为：Organza。质地透明或半透明的轻纱，多覆盖于缎布或丝绸(Silk)上面。法国人设计的婚纱多用欧根纱为主要原料。锦纶是聚酰胺纤维的商品名称，又称耐纶（Nylon）。英文名称Polyamide（简称PA），其基本组成物质是通过酰胺键—[NHCO]—连接起来的脂肪族聚酰胺。聚酰胺主要用于合成纤维，其最突出的优点是耐磨性高于其他所有纤维，比棉花耐磨性高10倍，比羊毛高20倍，在混纺织物中稍加入一些聚酰胺纤维，可大大提高其耐磨性；当拉伸至3-6%时，弹性回复率可达100%；能经受上万次折挠而不断裂。聚酰胺纤维的强度比棉花高1-2倍、比羊毛高4-5倍，是粘胶纤维的3倍。但聚酰胺纤维的耐热性和耐光性较差，保持性也不佳，做成的衣服不如涤纶挺括。另外，用于衣着的锦纶-66和锦纶-6都存在吸湿性和染色性差的缺点，为此开发了聚酰胺纤维的新品种——锦纶-3和锦纶-4的新型聚酰胺纤维，具有质轻、防皱性优良、透气性好以...
【技术保护点】
一种锦纶欧根纱的制备方法，其特征在于，包括以下步骤：A、将凹凸棒石和石墨烯在高速球磨机中高速研磨，得到纳米级混合粉末；B、将抗菌植物磨成粉状后，采用萃取法进行提取，得到抗菌植物提取液；C、在抗菌植物提取液中加入表面活性剂，搅拌均匀；D、将步骤A中的纳米级混合粉末加入步骤C的溶液中，搅拌均匀，并冷冻干燥，得到锦纶改性粉末；E、将聚酰胺6切片磨成粉后与步骤D中的锦纶改性粉末共混造粒得到改性锦纶纤维切片；F、将改性锦纶纤维切片干燥后，熔融纺丝得到改性锦纶纤维；G、将改性锦纶纤维制成锦纶欧根纱面料，即可。
【技术特征摘要】
1.一种锦纶欧根纱的制备方法，其特征在于，包括以下步骤：A、将凹凸棒石和石墨烯在高速球磨机中高速研磨，得到纳米级混合粉末；B、将抗菌植物磨成粉状后，采用萃取法进行提取，得到抗菌植物提取液；C、在抗菌植物提取液中加入表面活性剂，搅拌均匀；D、将步骤A中的纳米级混合粉末加入步骤C的溶液中，搅拌均匀，并冷冻干燥，得到锦纶改性粉末；E、将聚酰胺6切片磨成粉后与步骤D中的锦纶改性粉末共混造粒得到改性锦纶纤维切片；F、将改性锦纶纤维切片干燥后，熔融纺丝得到改性锦纶纤维；G、将改性锦纶纤维制成锦纶欧根纱面料，即可。2.如权利要求1所述的锦纶欧根纱的制备方法...
【专利技术属性】
技术研发人员：朱远昌，
申请(专利权)人：长兴博美纺织有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。