The invention discloses an imitated Anodizing Coating and a preparation method thereof, wherein the coating comprises the following raw materials by weight ratio: polyurethane acrylic resin 75; fluorocarbon resin 80; leveling agent 1.5; curing agent 4; electroplating silver paste 18; anti scratch agent 3.7; nano paste Beige 28 a. The manufacturing method includes the following steps: the polyurethane acrylic resin according to the predetermined proportion, leveling agent, solvent, electroplating silver paste stir until completely dissolved, add the fluorocarbon resin, curing agent, anti blowing agent, nano paste by fully mixing, spraying, drying, forming film on the surface of the product, which is equivalent to the effect of anodic oxidation film. The invention has the advantages that the imitation anodic oxidation coating of the present invention is equivalent to the paint with anodic oxidation texture and performance, and has the characteristics of short product coloring time, batch color difference stability, simple operation and the like.
【技术实现步骤摘要】
一种仿阳极氧化涂料及其制备方法
本专利技术涉及一种涂料，特别涉及一种仿阳极氧化涂料及其制备方法。
技术介绍
现有的阳极氧化是将金属或合金的制件作为阳极，采用电解的方法使其表面形成氧化物薄膜，该薄膜层中具有大量的极具吸附能力的微孔，可吸附染料，从而进行着色，该技术具有良好的耐腐蚀性，耐磨性及质感。但这种方式需要的时间很长，往往要几十分钟，而着色的颜色受着色机理，氧化膜厚度，电解着色速度的影响，很难把控批量一致性。
技术实现思路
本专利技术针对现有技术中存在的缺陷，现提供一种仿阳极氧化涂料及其制备方法，具有产品着色时间短，批差色差稳定，操作简单等特点（直接用喷枪喷涂即可）。为实现上述目的，本专利技术采用下述技术方案：一种仿阳极氧化涂料，由下列重量配比的原料制成:聚氨酯丙烯酸树脂75份；氟碳树脂80份；流平剂1.5份；、固化促进剂4份；电镀银浆18份；抗刮助剂3.7份；纳米色浆28份。所述仿阳极氧化涂料的制备方法如下：包括以下步骤：按预定比例将聚氨酯丙烯酸树脂，流平剂溶剂，电镀银浆搅拌至完全溶解，再加入氟碳树脂，固化促进剂，抗刮助剂，纳米色浆充分搅拌，经喷枪喷涂，干燥后，在...
【技术保护点】
一种仿阳极氧化涂料，其特征在于：由下列重量配比的原料制成: 聚氨酯丙烯酸树脂75份；氟碳树脂80份；流平剂1.5份；、固化促进剂4份；电镀银浆18份；抗刮助剂3.7份；纳米色浆28份。
【技术特征摘要】
1.一种仿阳极氧化涂料，其特征在于：由下列重量配比的原料制成:聚氨酯丙烯酸树脂75份；氟碳树脂80份；流平剂1.5份；、固化促进剂4份；电镀银浆18份；抗刮助剂3.7份；纳米色浆28份。2.权利要求1所述的仿阳极氧化涂料的...
【专利技术属性】
技术研发人员：王占庭，王辉，赵云鹏，
申请(专利权)人：安徽康瑞高科新材料技术工程有限公司，
类型：发明
国别省市：安徽,34