The invention discloses a method using single or double oxygen containing groups of emulsifier to prepare waterborne epoxy resin emulsion, relates to the technical field of waterborne epoxy resin emulsion, made the following quality percentage of raw materials: 40 epoxy resin 65%, emulsifier 6 20%, 12%, 0 propylene glycol methyl ether deionized water 35 40%. The invention of reactive epoxy emulsifier using the regular structure by phase inversion method of waterborne epoxy resin emulsion has good emulsifying effect and good stability, the particle size of the emulsion in 0.6 1.8um; and the epoxy equivalent reactive epoxy emulsifier is 500 2000 g / mol, using its structure containing epoxy group and amine curing agent and reaction stability in the cured product, so as to improve the coating formed by coating water resistance and salt fog resistance.
【技术实现步骤摘要】
利用含单或双环氧基团的乳化剂制备的水性环氧树脂乳液
：本专利技术涉及水性环氧树脂乳液
，具体涉及一种利用含单或双环氧基团的乳化剂制备的水性环氧树脂乳液。
技术介绍
：环氧树脂具有粘结性好、固化收缩率低、机械强度高、耐腐蚀性及耐溶剂性良好等优点，在化工、电器、建筑、航空等领域有着广泛的应用。传统的环氧树脂多为溶剂型环氧树脂，溶剂的使用会产生大量的挥发性有机化合物，污染环境且对人体健康造成不利影响。水性环氧树脂作为一种环境友好型产品，越来越受到人们关注。但是环氧树脂本身不溶于水，不能直接加水进行乳化，必须在其分子链中引入亲水基团或在体系中加入亲水亲油组分。目前，相反转法是一种适合工业化制备水性环氧树脂的方法。利用相反转法制备的水性环氧树脂不仅粒径小，稳定性好，成本低，并能避免传统外加小分子乳化剂存在的所制乳液容易破乳、不稳定且游离的小分子会降低涂料涂膜耐水性的问题。以环氧树脂分子主链作为亲油部分，接枝的亲水基团或亲水链段作为亲水部分，合成具有双亲性能的环氧树脂乳化剂，此种乳化剂与环氧树脂的分子结构相似，与环氧树脂相容性好，从而可提高环氧树脂水乳液的稳定性；并且乳...
【技术保护点】
利用含单或双环氧基团的乳化剂制备的水性环氧树脂乳液，其特征在于，由如下质量百分比的原料制成：
【技术特征摘要】
1.利用含单或双环氧基团的乳化剂制备的水性环氧树脂乳液，其特征在于，由如下质量百分比的原料制成：2.根据权利要求1所述的利用含单或双环氧基团的乳化剂制备的水性环氧树脂乳液，其特征在于，其制备方法为：将环氧树脂、乳化剂、丙二醇甲醚加热熔融，高速搅拌，待冷却至70℃后开始滴加去离子水，直至相反转得到稳定的乳液。3.根据权利要求1或2所述的利用含单或双环氧基团的乳化剂制备的水性环氧树脂乳液，其特征在于：所述乳化剂由如下质量百分比...
【专利技术属性】
技术研发人员：刘晓非，杜则冰，
申请(专利权)人：安徽艾珀希德化工科技有限公司，
类型：发明
国别省市：安徽,34