The invention provides a PVC foaming extrusion floor preparation process, and relates to the technical field of wood material production, mainly including mixing, extrusion, extrusion foaming and cooling process; the mixing process, the raw material components and components: PVC30 ~ 50%, 2 ~ 5%, foaming regulator filler 15 ~ 35% from 1 to 5%, lubricant foaming agent, 0.5 to 2%, above all the components of the processing aids; and meet 100%; foam material at the same time, the surface of the polymer material covered in foam substrate by CO extrusion machine. Waterproof, moisture-proof, solved the fundamental wood products on water wet and damp water environment perishable, expansion, strong plasticity, can be very simple to achieve personalized styling, fully embodies the personal style, no crack, no swelling, no deformation, no maintenance and maintenance, easy to clean, saving for the maintenance and maintenance cost.
【技术实现步骤摘要】
一种PVC发泡共挤地板制备工艺
：本专利技术涉及塑木材料生产
，尤其涉及一种PVC发泡共挤地板制备工艺。
技术介绍
：塑料包装废弃物已严重地污染了环境，影响了工农业生产，危害了人类健康和动植物的生存。世界塑料年产量已超过2亿吨，我国塑料包装材料2007年已超过1000万吨，这些塑料包装材料和容器经一次性使用后，大部分成了固体废弃物。塑料包装废弃物重量轻、体积大、数量多，难以降解，又不能随意焚化，大多被丢弃在铁路边、内河水域和城镇大街小巷，日积月累便成了触目惊心的“白色污染”带。据有关部门调查了解上海日产垃圾1000吨，塑料废弃物约占330吨；北京日产垃圾12000吨，塑料废弃物约占360吨；广州日产垃圾约6000吨，塑料垃圾约占200吨。我国采伐剩余物和造材剩余物约占林木生物量的40％,按照国务院批准的“十一五”期间森林采伐限额2.5亿m3/a计算,我国每年将产生约1.1亿吨的采伐、造材剩余物。另外,加工剩余物按原木的34.4％计算也有高达3210万m3的年产量。目前,虽然林业“三剩物”的利用已经引起人们的重视,但在世界范围内发展水平并不平衡。中国等发展中国...
【技术保护点】
一种PVC发泡共挤地板制备工艺，其特征在于：主要包括混料、挤出发泡、共挤、冷却定型生产过程；混料过程，所需的原料组分及组分量为：
【技术特征摘要】
1.一种PVC发泡共挤地板制备工艺，其特征在于：主要包括混料、挤出发泡、共挤、冷却定型生产过程；混料过程，所需的原料组分及组分量为：以上各组分量之和满足100％；混料过程，将料按配方混合，经过混料机高速搅拌，摩擦生热，至设定的工艺温度110～115℃后排入冷混，至设定工艺50℃后排料；挤出发泡过程，将混合好的原料加入挤出...
【专利技术属性】