一种FeS2‑RGO复合材料、制备方法及其应用技术
A FeS2 RGO composite material, preparation method and application thereof
The invention discloses a FeS2 RGO composite material, preparation method and application thereof. FeS2 RGO composite material of the invention is by graphene oxide dissolved in DMF aqueous solution, then adding nine hydrated ferric nitrate and thioacetamide, at 85 to 95 DEG C under stirring overnight, and then through the hydrothermal reduction of graphene oxide, after centrifugation, washing, freeze-dried, get calcined in hydrogen; FeS2 RGO composite material of the invention can be used for the electrocatalytic hydrogen evolution, because the low cost of raw materials, simple preparation method, the hydrogen evolution performance is good, good stability of catalyst, a good solution to the preparation of hydrogen now because of high cost, difficult to industrialization.
【技术实现步骤摘要】
一种FeS2-RGO复合材料、制备方法及其应用
本专利技术涉及产氢
，具体的说，涉及一种FeS2-RGO复合材料、制备方法及其应用。
技术介绍
能源是人类生存的根本，也是国家发展的根本。在国家的战略中，能源往往占有十分重要的地位，其决定了一个国家发展的深度与广度的同时，也决定了一个国家的兴衰。相对于太阳能、核能等新型可再生清洁能源，氢气具有制备条件相对容易、设备维护简单、绿色环保等优势。其燃烧时放出的热量大，产物为水，不污染环境，因此，作为一种可再生的绿色能源，氢气凭借其广泛的应用前景，进入了我们的视野，将氢气作为新型能源代替化石燃料，也成为了当今世界的研究热点。传统方法制备氢气主要包括水煤气法和石油裂解法等。然而，这些方法制备出的氢气纯度较低，同时需要消耗大量的化石原料，因此，以水为原料来制取氢气，包括光解水产氢和电解水产氢在内的新技术，正在得到人们的广泛关注。电解水制氢是一种安全性较高，效率较高的成熟制氢技术，然而在电解水制氢过程中，往往需要消耗巨大的电能，因此，现今电解水制氢的研究重点主要在如何降低电解能量方面，而作为电解水制氢中降低电解能量所用的最为...
【技术保护点】
一种FeS2‑RGO复合材料的制备方法，其特征在于，具体步骤如下：首先通过Hummer合成氧化石墨烯，然后将氧化石墨烯溶解在DMF中，接着依次加入九水合硝酸铁和硫代乙酰胺的水溶液，在85～95℃的温度下搅拌过夜，再通过水热反应还原氧化石墨烯，离心、洗涤、冻干以后，最后在氢气下煅烧，即得FeS2‑RGO复合材料；所述氧化石墨烯、九水合硝酸铁和硫代乙酰胺的质量比为(3～7)：(60～80)：(140～160)。
【技术特征摘要】
1.一种FeS2-RGO复合材料的制备方法，其特征在于，具体步骤如下：首先通过Hummer合成氧化石墨烯，然后将氧化石墨烯溶解在DMF中，接着依次加入九水合硝酸铁和硫代乙酰胺的水溶液，在85～95℃的温度下搅拌过夜，再通过水热反应还原氧化石墨烯，离心、洗涤、冻干以后，最后在氢气下煅烧，即得FeS2-RGO复合材料；所述氧化石墨烯、九水合硝酸铁和硫代乙酰胺的质量比为(3～7)：(60～80)：(140～160)。2.根据权利要求1...