The invention discloses a high strength and high elasticity copper alloy and a preparation method thereof, belonging to the field of nonferrous metal processing, in particular to a copper base elastic alloy. The high strength and high elastic copper alloy consists of the following components and content: Ni Co 4.8 ~ 7.6wt%, 0.05 ~ 0.10wt%, 2.3 ~ V 5.7wt%, Cr Mo 1.7 ~ 2.2wt%, 3.5 ~ 5.7wt%, 1.5 ~ Zn 2.3wt%, Mn Ti 1.2 ~ 2.3wt%, 0.7 ~ 2.5wt%, the rest is Cu. The tensile strength of the copper alloy can reach 1300MPa ~ 1600MPa, the elongation of 11.5% ~ 16%, and has very high fatigue strength, not less than 460MPa; and the copper alloy tensile strength and elongation after the fluctuation range are small, meet the plug 1.5N plug with more than 40000 times, available for electron elastic components.
【技术实现步骤摘要】
一种高强高弹性铜合金及其制备方法
本专利技术属于有色金属加工领域，具体涉及铜基弹性合金，尤其涉及一种高强高弹性铜合金及其制备方法。
技术介绍
高强高弹铜合金是弹性元件和电子元器件的关键材料之一，广泛应用在电子、通信汽车等领域。目前国内市场上铜基弹性合金以铍青铜和锡磷青铜等材料为主，铍青铜是一种优质弹性材料，但是也有其固有缺点，铍的氧化物或粉尘有毒，合金性能对热处理敏感，高温抗应力松弛能力差，不宜长时间在较高温度下工作。锡磷青铜属于应用最广泛的铜基弹性合金，但其弹性性能较低，耐疲劳性能差，仅应用于中低端弹性元件。普通家用墙壁插座或插排，要求插拔次数≥5000次，插拔力：1.5N(min)，一般锡磷青铜即可满足要求。对于人流量较大的户外或者公共场合，对插座使用频率极高，要求插拔次数≥40000次，插拔力：1.5N(min)，锡磷青铜在插拔30000次时会出现裂纹，因此不能满足户外或公共场合需求。专利201611036913.4《一种高强高弹CuNiSn合金材料及其制备方法》，该合金含有Ni8.5～10.5wt％、Sn1.8～2.8wt％、Co0.5～1.0wt％、B0...
【技术保护点】
一种高强高弹性铜合金，其特征在于由以下成分及含量熔炼而成：Ni 4.8～7.6wt％，Co 0.05～0.10wt％，V 2..3～5.7wt％，Cr 1.7～2.2wt％，Mo 3.5～5.7wt％，Zn 1.5～2.3wt％，Mn 1.2～2.3wt％，Ti 0.7～2.5wt％，余量为Cu。
【技术特征摘要】
1.一种高强高弹性铜合金，其特征在于由以下成分及含量熔炼而成：Ni4.8～7.6wt％，Co0.05～0.10wt％，V2..3～5.7wt％，Cr1.7～2.2wt％，Mo3.5～5.7wt％，Zn1.5～2.3wt％，Mn1.2～2.3wt％，Ti0.7～2.5wt％，余量为Cu。2.根据权利要求1所述的高强高弹性铜合金，其特征在于由以下成分及含量熔炼而成：Ni5.0～6.2wt％，Co0.07～0.09wt％，V3.2～5.4wt％，Cr1.8～2.0wt％，Mo4.0～5.1wt％，Zn1.7～2.0wt％，Mn1.6～2.0wt％，Ti1.2～1.9wt％，余量为Cu。3.一种权利要求1或2所述高强高弹性铜合金的制备方法，其特征在于包括如下步骤：(1)准备配料，(2)真空感应熔炼，(3)均匀化热处理，(4)铣面、粗轧，(5)热轧，(6)固溶退火处理，(7)合金冷变形，(8)时效热处理，其中步骤(2)所述真空感应熔炼具体为：将原料加熔炼炉内，进行抽真空，至真空度≤10-2Pa，充入氩气进行保护，熔炼温度1550～1...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。