The invention discloses a reinforced composite silk, the weight ratio of ingredients including: silk fiber 6 10, tussah silk long fiber 6 10, castor silk fiber with 4 6 copies, cassava silk fibers 4 6 copies, 3 copies of the 2 viscose fiber, acetate fiber 2 3 copies, 3 copies of 2 copper ammonia fiber. By the way, the present invention reinforced composite silk by using natural silk fiber as the main raw material of silk, wearing comfortable, soft texture, good air permeability, good moisture absorption, good heat preservation, while adding amount of artificial fiber modified silk natural silk, improve the strength and toughness in reinforced the popularity of composite silk has a broad market prospect.
【技术实现步骤摘要】
一种增强型复合丝绸
本专利技术涉及丝绸领域,特别是涉及一种增强型复合丝绸。
技术介绍
现有的丝绸大多采用天然蚕丝作为原料,在强度和韧性方面性能较差,日常使用时易形变、易拉扯断裂,不利于长久使用。
技术实现思路
本专利技术主要解决的技术问题是提供一种增强型复合丝绸,通过采用天然蚕丝纤维作为丝绸的主要原材料,穿着舒适、质地轻柔、透气性好、吸湿性好、保暖性好,同时添加适量的人造纤维实现对丝绸的改性,改善了天然丝绸的强度和韧性,在增强型复合丝绸的普及上有着广泛的市场前景。为解决上述技术问题,本专利技术提供一种增强型复合丝绸,成分的重量配比包括:桑蚕丝长纤维6-10份,柞蚕丝长纤维6-10份,蓖麻蚕丝短纤维4-6份,木薯蚕丝短纤维4-6份,粘胶纤维2-3份,醋酸纤维2-3份,铜氨纤维2-3份。在本专利技术一个较佳实施例中,成分的重量配比包括0-2份桑蚕丝短纤维。在本专利技术一个较佳实施例中,成分的重量配比包括0-2份柞蚕丝短纤维。在本专利技术一个较佳实施例中,成分的重量配比包括0-2份竹炭纤维。本专利技术的有益效果是:本专利技术增强型复合丝绸通过采用天然蚕丝纤维作为丝绸的主要原材料,穿着舒适、质地轻柔、透气性好、吸湿性好、保暖性好,同时添加适量的人造纤维实现对丝绸的改性,改善了天然丝绸的强度和韧性,在增强型复合丝绸的普及上有着广泛的市场前景。具体实施方式下面将对本专利技术实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本专利技术的一部分实施例,而不是全部的实施例。基于本专利技术中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例 ...
【技术保护点】
一种增强型复合丝绸,其特征在于,成分的重量配比包括:桑蚕丝长纤维6‑10份,柞蚕丝长纤维6‑10份,蓖麻蚕丝短纤维4‑6份,木薯蚕丝短纤维4‑6份,粘胶纤维2‑3份,醋酸纤维2‑3份,铜氨纤维2‑3份。
【技术特征摘要】
1.一种增强型复合丝绸,其特征在于,成分的重量配比包括:桑蚕丝长纤维6-10份,柞蚕丝长纤维6-10份,蓖麻蚕丝短纤维4-6份,木薯蚕丝短纤维4-6份,粘胶纤维2-3份,醋酸纤维2-3份,铜氨纤维2-3份。2.根据权利要求1所述的增强型复...