The utility model relates to a solid welding wire for high strength steel gas shielded arc welding, which belongs to the technical field of welding materials. The chemical components by mass percent: C:0.06 0.15%, Si:0.60 1%, Mn:1.50 2%, P = 0.025%, S = 0.020%, Ni:0.10 0.60%, Cr:0.40 0.80%, Cu 0.25%, V:0.02 0.10% Ti:0.08 0.25%,, B:0.002 0.008%, O = 0.0070%, N = 0.0070%, the rest is iron impurities and the inevitable. The utility model has the advantages that the mechanical property is better than that of the base material; the welding operation is excellent; the operation process window is wide; the industrialized production route is mature and efficient; the processing and manufacturing cost economy.
【技术实现步骤摘要】
一种高强钢气体保护电弧焊用实心焊丝
本专利技术属于焊接材料
，特别涉及一种高强钢气体保护电弧焊用实心焊丝(以下简称实心气保焊丝)。尤其提供了一种熔敷金属抗拉强度Rm≥650MPa的实心气保焊丝及其原料盘条，可用于工程机械、建筑、桥梁等领域相应高强钢板的焊接。
技术介绍
近年来，焊接材料的品种结构发生了较大变化，手工电焊条耗费量虽然也在增长，但占焊材消费总量的比例由10年前的近80％降至50％以下，而自动焊所需的各种类焊丝比例则相应增长至50％以上，尤其实心气保焊丝，具有操作灵活、高效高能的优势，逐步成为替代手工电焊条的主要焊接材料，现年表观消费量基本稳定在150万吨左右，而随着我国劳动力成本持续上升、熟练焊工短缺以及焊接效率的提高等形势趋势，焊接自动化的进程明显加快，预计今后几年，我国焊接自动化水平仍将稳步提升，以焊丝为代表的半自动化、自动化焊接材料的比例将持续提高。除了产品类型的改变，产品等级也在提升，随着战备性新型产业的发展，高端装备制造业所需的高端钢材逐年增量，例如海工、核电和煤电及水电工程、大型石化设备制造、桥梁工程等，大型工程机械也要配套发展。在这...
【技术保护点】
一种高强钢气体保护电弧焊用实心焊丝，其特征在于，化学成分按质量百分比为：C：0.06‑0.15％，Si：0.60‑1.00％，Mn：1.50‑2.00％，P≤0.025％，S≤0.020％，Ni：0.10‑0.60％，Cr：0.40‑0.80％，Cu≤0.25％，V：0.02‑0.10％，Ti：0.08‑0.25％，B：0.002‑0.008％，O≤0.0070％，N≤0.0070％，其余为铁和不可避免的杂质。
【技术特征摘要】
1.一种高强钢气体保护电弧焊用实心焊丝，其特征在于，化学成分按质量百分比为：C：0.06-0.15％，Si：0.60-1.00％，Mn：1.50-2.00％，P≤0.025％，S≤0.020％，Ni：0.10-0.60％，Cr：0.40-0.80％，Cu≤0.25％，V：0.02-0.10％，Ti：0.08-0.25％，B：0.002-0.008％，O≤0.0070％，N≤0.0070％，其余为铁和不可避免的杂质。2.根据权利要求1所述的实心焊丝，其特征在于，所用原料盘条元素含量与焊丝要求相同。3.根据权利要求1所述的实心焊丝，其特征在于，所述的C含量为0.06-0.10wt％。4.根据权利要求1所述的实心焊...
【专利技术属性】
技术研发人员：陈涛，张飞虎，易敏，吕迺冰，佟倩，马跃，孙齐松，