The invention discloses an air cooling device of corrosion inhibitor, the composition of raw materials including: chlorinated compounds 5 ~ 15, 0 ~ 15 organic amines, polyamines 0 ~ 5, 0 ~ 20 alcohol and deionized water from 45 to 70, the number of copies for quality copies. The air cooling device corrosion inhibitor can effectively disperse the adhesion on the pipe wall, ammonium chloride and ammonium thiochloride ferrous sulfide salt deposit and formation and prevent new fouling, prevent the occurrence of corrosion under the scale; also has a good inhibitory effect on H2S - NH3 - HCl - H2O through the protective film is formed on the corrosion; the metal surface effectively, can reduce the corrosion of high pressure air cooler fouling; the application of air cooling device corrosion inhibitor has good thermal stability, good chemical stability, low toxicity, no smell, no side effects on the subsequent processing of oil.
【技术实现步骤摘要】
一种空冷装置缓蚀剂、其制备方法及其应用
本专利技术涉及一种空冷装置缓蚀剂、其制备方法及其应用，属于防腐领域。
技术介绍
近年来，随着成品油标准的逐步提高，各炼厂普遍采用加氢处理来提高油品的质量，然而目前加工的原油逐步向高硫、高酸的趋势发展，使得加氢装置受到加氢反应产物中H2S、NH3和HCI的严重腐蚀，且它们能相互作用发生反应生成硫氢化铵和氯化铵等。硫氢化铵和氯化铵的升华温度比较低，因此流出物在高压空冷器内被冷却的过程中，常在空冷管束和下游设备管道中发生硫氢化铵和氯化铵盐等的沉积、结垢，造成设备管道严重的堵塞和腐蚀。
技术实现思路
为了解决现有技术中管道堵塞和腐蚀等缺陷，本专利技术提供一种空冷装置缓蚀剂、其制备方法及其应用。为解决上述技术问题，本专利技术所采用的技术方案如下：一种空冷装置缓蚀剂，其原料组分包括：氯代物5～15份，有机胺0～15份，多胺0～5份，醇类0～20份和去离子水45～70份，所述份数为质量份数。上述空冷装置缓蚀剂能有效分散粘附在管壁上的硫氢化铵、氯化铵以及硫化亚铁等盐垢，并阻止新的盐垢的形成，防止垢下腐蚀的发生；对H2S—NH3—HCl—H2O型...
【技术保护点】
一种空冷装置缓蚀剂，其特征在于：其原料组分包括：氯代物5～15份，有机胺0～15份，多胺0～5份，醇类0～20份和去离子水45～70份，所述份数为质量份数。
【技术特征摘要】
1.一种空冷装置缓蚀剂，其特征在于：其原料组分包括：氯代物5～15份，有机胺0～15份，多胺0～5份，醇类0～20份和去离子水45～70份，所述份数为质量份数。2.如权利要求1所述的空冷装置缓蚀剂，其特征在于：氯代物为氯辛烷、氯代十二烷、氯代十四烷或氯化苄中的至少一种。3.如权利要求1或2所述的空冷装置缓蚀剂，其特征在于：有机胺为十二烷基二甲基叔胺、十四烷基二甲基叔胺、十六烷基二甲基叔胺或N,N-二甲基苄胺中的至少一种。4.如权利要求1或2所述的空冷装置缓蚀剂，其特征在于：多胺为二乙烯三胺、三乙烯四胺、四乙烯五胺或五乙烯六胺中的至少一种。5.如权利...
【专利技术属性】
技术研发人员：颜梦秋，沙玉英，葛圣才，戴泽青，
申请(专利权)人：金浦新材料股份有限公司，
类型：发明
国别省市：江苏,32