一种导电油墨及其制备方法技术

本发明专利技术公开了一种导电油墨及其制备方法，导电油墨包括如下重量份的原料：水性高分子树脂30‑50份；乙炔炭黑15‑25份；水12‑20份；乙醇8‑12份；乙二醇丁醚3‑8份；硅烷表面处理剂4‑9份；防静电剂2‑5份；分散剂1‑3份；纳米金属粒子3‑15份。本发明专利技术的导电油墨的粘度低，喷涂适应性好，附着力好，适用于软板和凹板印刷，能够提高印刷效率，并且其电阻率低、导电性能稳定；导电油墨的制备方法简单，易于批量化生产。

Conductive ink and preparation method thereof

The invention discloses a conductive ink and preparation method thereof, conductive ink comprises the following raw materials: water soluble polymer resin 30 50; 15 acetylene black 25; water 12 20; 8 ethanol 12; ethylene glycol butyl ether 3 8; silane surface treatment agent 4 9; antistatic agent 2 5; dispersant 1 3; 3 15 nano metal particles. The conductive ink of this invention has low viscosity, spraying, good adaptability, good adhesion, suitable for soft board and gravure printing, can improve the efficiency, and the low resistivity, stable electrical conductivity; conductive ink has the advantages of simple preparation method, easy mass production.

【技术实现步骤摘要】
一种导电油墨及其制备方法
本专利技术涉及化工原料
，尤其涉及一种导电油墨及其制备方法。
技术介绍
触摸屏是人机交互的重要媒介之一，随着触控产品的应用升级，人们对触摸屏的性能要求也越来越高，触摸屏逐渐向功能多样化和大尺寸化等方向发展。电容触摸屏是利用人体的电流感应进行工作的，电容触摸屏的生产制作过程中通常会用到导电油墨。导电油墨作为一种新型的特种功能高分子材料，主要由基体树脂和导电填料组成。传统的导电油墨主要是油溶性的，导电油墨本身毒性较大，生产过程危险，并且溶剂对环境污染严重，难以处理。随着人们环保意识的提高，出现了以水为溶剂的水溶性导电油墨，如何提高水溶性导电油墨的导电稳定性一级附着力等逐渐成为人们的研究课题。
技术实现思路
本专利技术所要解决的技术问题是：提供一种导电性能稳定、附着力好的导电油墨及其制备方法。为了解决上述技术问题，本专利技术采用的技术方案为：一种导电油墨，包括如下重量份的原料：水性高分子树脂30-50份；乙炔炭黑15-25份；水12-20份；乙醇8-12份；乙二醇丁醚3-8份；硅烷表面处理剂4-9份；防静电剂2-5份；分散剂1-3份；纳米金属粒子3-15份。本专本文档来自技高网...

【技术保护点】
一种导电油墨，其特征在于，包括如下重量份的原料：水性高分子树脂30‑50份；乙炔炭黑15‑25份；水12‑20份；乙醇8‑12份；乙二醇丁醚3‑8份；硅烷表面处理剂4‑9份；防静电剂2‑5份；分散剂1‑3份；纳米金属粒子3‑15份。

【技术特征摘要】
1.一种导电油墨，其特征在于，包括如下重量份的原料：水性高分子树脂30-50份；乙炔炭黑15-25份；水12-20份；乙醇8-12份；乙二醇丁醚3-8份；硅烷表面处理剂4-9份；防静电剂2-5份；分散剂1-3份；纳米金属粒子3-15份。2.根据权利要求1所述的导电油墨，其特征在于，所述水性高分子树脂为聚丙烯酰胺、聚丙烯酸和聚乙烯吡咯烷酮中的至少一种。3.根据权利要求1所述的导电油墨，其特征在于，所述硅烷表面处理剂包括硅烷偶联剂。4.根据权利要求1所述的导电油墨，其特征在于，所述分散剂为酚醛树脂、聚氨酯、脲醛树脂、三聚氰胺甲醛树脂、糠醛树脂、不饱和聚酯、氯丁橡...