一种透气透湿面料制造技术
Breathable moisture permeable fabric
The invention discloses a breathable fabric, the fabric is woven by warp and weft yarn into fabric after dyeing and finishing is made; the warp and weft yarn and B yarn were A according to the 1:1 arrangement than through picking; the A yarn and B yarn are composite yarn by siro spinning and Siro Phil spun regenerated cellulose fiber yarn and water-soluble fiber spirally twisted; the A yarn and B yarn twist, twist to the contrary; the dyeing including singeing, desizing, shaping, printing or dyeing and softening finishing process, the desizing process the temperature is 80 DEG C 100. The present invention not only has good ventilation and moisture permeability, but also feels light and soft, and the fabric surface is smooth and stable.
【技术实现步骤摘要】
一种透气透湿面料
本专利技术属于家用纺织品
，具体涉及一种透气透湿面料。
技术介绍
夏季床品面料要求透气透湿、柔软舒适，面料透气透湿性与织物中孔隙大小的分布特征有关，具体影响因素有纤维性质、纱线结构和织物结构以及环境条件等。常用于夏季床品面料的再生纤维素纤维具有吸湿性、透气性和亲肤性较好，但是吸收人体湿气后，纤维素纤维吸湿膨胀，纤维直径变粗导致面料透气性变差，手感发硬，且由于纤维吸湿滞后性，吸湿后水分难以排出，面料粘在皮肤表面，人体感觉闷热不舒适。织物采用透孔组织或纱罗组织进行织造，表面可实现均匀或清晰分布的小孔，有利于改善面料通透性，透孔组织透孔经水洗或力作用下孔结构容易变形，稳定性差；纱罗组织透孔结构稳定，但孔径较大且质地轻薄。现有的技术采用透孔组织与退维处理来获得高透气性，比如CN104342818公开了一种透气织物，采用透孔组织使织物表面分布孔洞，采用双层组织或三层组织结构获得垂直通道。通过透孔组织、多层结构构造通道，不适用于要求布面柔软轻透、紧密结实、耐用性好的床品面料。比如CN102337621A公开了一种吸水透气性织物，采用碱减量加工方法使纱线...
【技术保护点】
一种透气透湿面料，其特征在于：由经纱和纬纱交织成坯布后经染整制成；所述经纱与纬纱均为A纱与B纱按1:1的排列比进行穿经投纬；所述A纱和B纱均是采用赛络纺或赛络菲尔纺将再生纤维素纤维单纱与水溶性纤维呈螺旋状捻合而成的复合纱；所述A纱和B纱的捻度相同、捻向相反；所述染整包括烧毛、退浆、定型、印花或染色、柔软整理的工序，其中，退浆工序的温度为80‑100℃。
【技术特征摘要】
1.一种透气透湿面料，其特征在于：由经纱和纬纱交织成坯布后经染整制成；所述经纱与纬纱均为A纱与B纱按1:1的排列比进行穿经投纬；所述A纱和B纱均是采用赛络纺或赛络菲尔纺将再生纤维素纤维单纱与水溶性纤维呈螺旋状捻合而成的复合纱；所述A纱和B纱的捻度相同、捻向相反；所述染整包括烧毛、退浆、定型、印花或染色、柔软整理的工序，其中，退浆工序的温度为80-100℃。2.根据权利要求1所述的透气透湿面料，其特征在于：所述复合纱中水溶性纤维的含量百分比为15-50%。3.根据权利要求1所述的透...
【专利技术属性】
技术研发人员：肖俐，陈红霞，陆鹏，丁可敬，
申请(专利权)人：江苏金太阳纺织科技股份有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。