本发明专利技术公开了一种无机粘结剂及其制备方法和制备混合球团的方法。该无机粘结剂的制备方法包括：(1)将高铝熟料粉、磷酸和水进行混合，以便得到混合物料；(2)将所述混合物料与石墨粉和氨水混合，以便得到无机粘结剂。该无机粘结剂具有良好的耐高温性能，且制备成本低廉，同时采用该无机粘结剂制备的混合球团的冷态抗压强度达600N以上，1000摄氏度热解后的抗压强度达500N以上。

Inorganic binder and preparation method thereof and process for preparing mixed pellets

The invention discloses an inorganic binder and a preparation method thereof and a method for preparing a mixed pellet. Including the preparation method of the inorganic binder: (1) the high alumina clinker powder, phosphoric acid and water are mixed, in order to get the mixed material; (2) the material mixed with graphite powder and ammonia water mixture, in order to obtain the inorganic binder. The inorganic binder has good heat resistance and low preparation cost, at the same time, the cold compression strength of the inorganic binder prepared by mixed pellet was more than 600N, the compressive strength of 1000 degrees Celsius after pyrolysis of more than 500N.

【技术实现步骤摘要】
无机粘结剂及其制备方法和制备混合球团的方法
本专利技术属于煤炭成型领域，具体而言，本专利技术涉及无机粘结剂及其制备方法和制备混合球团的方法。
技术介绍
中国长焰煤储量巨大、价格低廉，但是其利用存在效率较低、浪费严重等问题。目前，块状长焰煤利用率较高，但是同时产生大量粉末状长焰煤粉，这不仅造成巨大的资源浪费，而且产生了一定的环境污染，因此，粉末状长焰煤的利用迫在眉睫。传统电石行业主要采用块状煤炭和块状生石灰为原料生产电石，但是该生产方式效率低下，这主要是由于块状煤炭和块状生石灰接触面积小、反应速度慢。然而，粉末状煤炭和粉末状生石灰却能有效克服这一缺点，两者接触面积大，在高温下制备电石的反应快，能有效节约能源。粉末状煤炭和粉末状生石灰制备的球团需要具有良好的冷态强度以保证能顺利进入旋转床，同时其也需要具有良好的热态强度，以保证热解后的球团具有能进入电炉的强度。现有制备上述球团的技术中，主要采用有机粘结剂，加入量较多，成本高，且成型所需的能耗、原料成本高。因此，现有生产电石的技术有待进一步改进。
技术实现思路
本专利技术旨在至少在一定程度上解决相关技术中的技术问题之一。为此，本专利技术的一个目本文档来自技高网...

【技术保护点】
一种制备无机粘结剂剂的方法，其特征在于，包括：(1)将高铝熟料粉、磷酸和水进行混合，以便得到混合物料；(2)将所述混合物料与石墨粉和氨水混合，以便得到无机粘结剂。

【技术特征摘要】
1.一种制备无机粘结剂剂的方法，其特征在于，包括：(1)将高铝熟料粉、磷酸和水进行混合，以便得到混合物料；(2)将所述混合物料与石墨粉和氨水混合，以便得到无机粘结剂。2.根据权利要求1所述的方法，其特征在于，在步骤(1)中，所述高铝熟料粉与所述磷酸、所述水的质量比为100：(5～10)：(20～40)。3.根据权利要求1或2所述的方法，其特征在于，在步骤(1)中，所述磷酸的质量浓度为80～90％。4.根据权利要求3所述的方法，其特征在于，在步骤(1)中，所述混合物料的pH值为1～2。5.根据权利要求1所述的方法，其特征在于，在步骤(2)中，所述混合物料与所述石墨粉的质量比为100：(2～5)。6.根据权利要求1或5所述的方法，其特征在于，在...

【专利技术属性】
技术研发人员：夏碧华，邓鑫，高建，吴道洪，
申请(专利权)人：神雾环保技术股份有限公司，
类型：发明
国别省市：北京,11