制备混合球团的方法技术
Process for preparing mixed pellets
The invention discloses a method, a preparation mixed pellet includes: (1) the inorganic binder mixed with colloidal silica and water, in order to obtain the mixed slurry; (2) the mixed slurry was mixed with long flame coal and limestone, in order to get the mixed material; (3) the mixed material is molded and solidified to obtain mixed pellet, which, in step (1), the inorganic binder for fused silica and Magnesium Sulfate in 1600 ~ 1700 degrees Celsius under reaction. As a result, the cold compressive strength of the mixed pellet obtained by the method is above 600N, and the compressive strength is 1000 degrees Celsius after pyrolysis, and the utility model has good high-temperature resistance performance.
【技术实现步骤摘要】
制备混合球团的方法
本专利技术属于煤炭成型领域，具体而言，本专利技术涉及制备混合球团的方法。
技术介绍
中国长焰煤储量巨大、价格低廉，但是其利用存在效率较低、浪费严重等问题。目前，块状长焰煤利用率较高，但是同时产生大量粉末状长焰煤粉，这不仅造成巨大的资源浪费，而且产生了一定的环境污染，因此，粉末状长焰煤的利用迫在眉睫。传统电石行业主要采用块状煤炭和块状生石灰为原料生产电石，但是该生产方式效率低下，这主要是由于块状煤炭和块状生石灰接触面积小、反应速度慢。然而，粉末状煤炭和粉末状生石灰却能有效克服这一缺点，两者接触面积大，在高温下制备电石的反应快，能有效节约能源。粉末状煤炭和粉末状生石灰制备的球团需要具有良好的冷态强度以保证能顺利进入旋转床，同时其也需要具有良好的热态强度，以保证热解后的球团具有能进入电炉的强度。现有制备上述球团的技术中，主要采用有机粘结剂，加入量较多，成本高，且成型所需的能耗、原料成本高。因此，现有生产电石的技术有待进一步改进。
技术实现思路
本专利技术旨在至少在一定程度上解决相关技术中的技术问题之一。为此，本专利技术的一个目的在于提出一种制备混合球团的...
【技术保护点】
一种制备混合球团的方法，其特征在于，包括：(1)将无机粘结剂与胶体二氧化硅和水混合，以便得到混合浆体；(2)将所述混合浆体与长焰煤粉和石灰石粉进行混合，以便得到混合物料；(3)将所述混合物料进行成型和固化处理，以便得到混合球团，其中，在步骤(1)中，所述无机粘结剂为熔融氧化硅和硫酸镁在1600～1700摄氏度下反应得到。
【技术特征摘要】
1.一种制备混合球团的方法，其特征在于，包括：(1)将无机粘结剂与胶体二氧化硅和水混合，以便得到混合浆体；(2)将所述混合浆体与长焰煤粉和石灰石粉进行混合，以便得到混合物料；(3)将所述混合物料进行成型和固化处理，以便得到混合球团，其中，在步骤(1)中，所述无机粘结剂为熔融氧化硅和硫酸镁在1600～1700摄氏度下反应得到。2.根据权利要求1所述的方法，其特征在于，所述熔融氧化硅与所述硫酸镁的混合质量比为1：(1.1～2)。3.根据权利要求1所述的方法，其特征在于，在步骤(1)中，所述无机粘结剂与所述胶体二氧化硅和所述水的混合质量比为1：(0.2～0.4)：(0.2～0.4...
【专利技术属性】
技术研发人员：夏碧华，邓鑫，高建，吴道洪，
申请(专利权)人：神雾环保技术股份有限公司，
类型：发明
国别省市：北京,11