The invention discloses a hard asphalt modified with a high Yandu, made in accordance with the following raw materials in weight portion: 130 petroleum asphalt 140, methyl silicone rubber powder 10 14, methyl vinyl silicone rubber powder 18 22 copies, 11 copies of 15 modified kaolin, BARATE 5 9 A, sulfated castor oil 12 15, three 5 trimellitic anhydride 8, alkyl phenol polyoxyethylene ether 2 5 allyl methacrylate, 3 6 copies, 8 copies of 4 sodium thioglycolate. Modified hard asphalt and preparation method of the invention also discloses the high Yandu. The modified hard asphalt prepared by the invention has high ductility, good high-temperature stability and low temperature crack resistance, and has important market value and social value.
【技术实现步骤摘要】
一种高延度的改性硬质沥青及其制备方法
本专利技术涉及沥青材料
，具体是一种高延度的改性硬质沥青及其制备方法。
技术介绍
沥青是常用于制备铺路和屋顶材料的材料。在道路建造和道路铺设工业中，成熟实用的方法是利用热的流体沥青涂覆骨料材料，例如沙子、砂砾、碎石或其混合物，在其还热的时候将涂覆的材料在路基或先前建造的道路上铺展为均匀层，并通过重型压路机滚压来将均匀层压实，以形成表面光滑的道路。改革开放以来中国的经济一直保持着高速的增长，公路交通建设突飞猛进，我国道路沥青生产企业也得到了迅猛发展。尤其是重交沥青和改性沥青实现了由无到有、由小到大、由少到多的质的飞跃，为我国道路建设做出了巨大贡献。然而沥青的发展规模同我们国内市场的需求相比较，中国沥青市场仍然处于供不应求的状态，尤其是那些高端的改性沥青市场，更是有巨大的市场空缺。现有的改性沥青材料普遍存在无法兼顾高温稳定性和低温抗裂性的缺陷，影响沥青的使用寿命。
技术实现思路
本专利技术的目的在于提供一种高延度的改性硬质沥青及其制备方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种高延度的改...
【技术保护点】
一种高延度的改性硬质沥青，其特征在于，由以下按照重量份的原料制成：石油沥青130‑140份、甲基硅橡胶粉10‑14份、甲基乙烯基硅橡胶粉18‑22份、改性高岭土11‑15份、偏硼酸钡5‑9份、硫酸化蓖麻油12‑15份、偏苯三酸酐5‑8份、烷基苯酚聚氧乙烯醚2‑5份、甲基丙烯酸烯丙酯3‑6份、巯基乙酸钠4‑8份。
【技术特征摘要】
1.一种高延度的改性硬质沥青，其特征在于，由以下按照重量份的原料制成：石油沥青130-140份、甲基硅橡胶粉10-14份、甲基乙烯基硅橡胶粉18-22份、改性高岭土11-15份、偏硼酸钡5-9份、硫酸化蓖麻油12-15份、偏苯三酸酐5-8份、烷基苯酚聚氧乙烯醚2-5份、甲基丙烯酸烯丙酯3-6份、巯基乙酸钠4-8份。2.根据权利要求1所述的高延度的改性硬质沥青，其特征在于，由以下按照重量份的原料制成：石油沥青133-138份、甲基硅橡胶粉11-13份、甲基乙烯基硅橡胶粉19-21份、改性高岭土12-14份、偏硼酸钡6-8份、硫酸化蓖麻油13-14份、偏苯三酸酐6-7份、烷基苯酚聚氧乙烯醚3-4份、甲基丙烯酸烯丙酯4-5份、巯基乙酸钠5-7份。3.根据权利要求2所述的高延度的改性硬质沥青，其特征在于，由以下按照重量份的原料制成：石油沥青135份、甲基硅橡胶粉12份、甲基乙烯基硅橡胶粉20份、改性高岭土13份、偏硼酸钡7份、硫酸化蓖麻油13份、偏苯三酸酐7份、烷基苯酚聚氧乙烯醚4份、甲基丙烯酸烯丙酯5份、巯基乙酸钠6份。4.根据权利要求1所述的高延度的改性硬质沥青，其特征在于，所述改性高岭土通过以下步骤获得：将高岭土与同等重量的10%柠檬酸水溶...