The invention discloses a rice cooker ceramic liner is not easy to paste pot, the liner comprises a liner shell and inner layer and inner liner, the liner layer is a metal layer, the outer layer of the inner liner for ordinary ceramic layer, which is characterized in that the inner liner is prepared from the following parts by weight: 50 aluminum nitride - 70, Y2O3 - 2, La2O3 1 2 - 3, SiO2 - 15, B2O3 10 10 ~ 20, 1 ~ 1.5 nm SnO2, MnO2 3 ~ 5. The inner layer of the ceramic liner of the invention has superior thermal conductivity, and the coefficient of linear expansion is close to the linear expansion coefficient of the metal inner liner, and the matching degree is good, and the cracking is not easy to occur.
【技术实现步骤摘要】
不易糊锅的电饭煲陶瓷内胆
本专利技术属于陶瓷材料领域，具体涉及一种不易糊锅的电饭煲陶瓷内胆。
技术介绍
内胆是电饭煲最重要的组成部分，对选购电饭煲起着决定性作用。内胆材质有铝合金、不锈钢、陶瓷。铝合金内胆很薄，外部涂覆不粘锅涂层，随着使用时间的延长，经常出现涂层脱落的现象，而铝本身对人体有伤害，因此不建议使用铝合金内胆。不锈钢内胆价格稍贵，但不会出现涂层脱落的问题，不过清洗不方便。陶瓷内胆则是采用纯天然无机物，避免了涂层和金属内胆在加热过程中对食物的二次污染。陶瓷内胆是应用于电饭煲的新技术，陶晶技术攻克了以往陶瓷表面处理技术中熔点、两种材料结合难、材料不嵌合等技术难关。在电饭煲内胆表面成功涂覆一层陶瓷材料陶瓷内胆经过一千四五百度的高温烧炼，具有稳定的保温性能。
技术实现思路
本专利技术要解决的技术问题是提供一种不易糊锅的电饭煲陶瓷内胆。本专利技术提供的技术方案是一种不易糊锅的电饭煲陶瓷内胆不易糊锅的电饭煲陶瓷内胆，该内胆包括内胆外层、内胆中层、内胆内层，所述内胆中层为金属层，内胆外层为普通陶瓷层，所述内胆内层由以下重量份的原料制成：氮化铝50～70份、Y2O31～2份...
【技术保护点】
不易糊锅的电饭煲陶瓷内胆，该内胆包括内胆外层、内胆中层、内胆内层，所述内胆中层为金属层，内胆外层为普通陶瓷层，其特征在于：所述内胆内层由以下重量份的原料制成：氮化铝50～70份、Y2O3 1～2份、La2O3 2～3份、SiO2 10～15份、B2O3 10～20份、纳米SnO2 1～1.5份、MnO2 3～5份。
【技术特征摘要】
1.不易糊锅的电饭煲陶瓷内胆，该内胆包括内胆外层、内胆中层、内胆内层，所述内胆中层为金属层，内胆外层为普通陶瓷层，其特征在于：所述内胆内层由以下重量份的原料制成：氮化铝50～70份、Y2O31～2份、La2O32～3份、SiO210～15份、B2O310～20份、纳米SnO21～1.5份、MnO23～5份。2.根据权利要求1所述的不易糊锅的电饭煲陶瓷内胆，其特征在于：所述氮化铝是采用Al2O3粉末与炭黑粉末经过球磨混合，在流动的氮气气氛中以氧化钙为催化剂，在1500～1700℃下反应生成；反应完成后，在700～800℃的...