The invention relates to a preparation method of a kind of activated carbon, with walnut shell as raw material, the walnut shell crushing and sieving, soaking in phosphoric acid solution and then added to the 16 24h, walnut shell with phosphoric acid solution weight ratio 1:3 6, filtration; heating activation residue in the muffle furnace will filter get in, and then cooled to room temperature, get the activator; the activator of pickling, and washing to neutral, is finally sieved. The method has the advantages of simple process, no wood as raw material, waste walnut shell as raw material, wide raw material source, low cost, and ecological environment protection, and the activated carbon produced by the invention has good adsorption effect.
【技术实现步骤摘要】
一种活性炭的制备方法
本专利技术涉及一种活性炭的制备方法,属于精细化工
技术介绍
活性炭是一种具有丰富孔隙结构和巨大比表面积的碳质吸附材料,它其有吸附能力强、化学稳定性好、力学强度高,且可方便再生等特点,被广泛应用于工业、农业、国防、交通、医药卫生、环境保护等领域,其需求量随着社会发展和人民生活水平提高,呈逐年上升的趋势,尤其是近年来随着环境保护要求的日益提高,使得国内外活性炭的需求量越来越大,逐年增长。目前,活性炭多采用木材为原料,原料比较贵、生产工艺比较复杂,并且这无疑将造成大量森林被砍伐,严重破坏生态。因此寻找廉价的原料和简单的生产工艺是十分必要的。
技术实现思路
本专利技术的目的是解决现有技术中活性炭的制备工艺存在的不足,提供一种活性炭的制备方法,其不以木材为原料,成本低、工艺简单,制得的活性炭吸附效果好。技术方案一种活性炭的制备方法,包括如下步骤:(1)以山核桃壳为原料,将山核桃壳破碎后过筛,然后加入到磷酸溶液中浸泡16-24h,过滤;(2)将过滤得到的滤渣置于马弗炉中加热活化,然后冷却至室温,得到活化物;(3)将活化物酸洗,再水洗至中性,最后过筛,即得;步骤(1)中,所述山核桃壳与磷酸溶液的重量比为1:3-6。进一步,步骤(1)中,所述磷酸溶液的浓度为35-55wt%。进一步,步骤(1)中,所述过筛为过30目筛。进一步,步骤(2)中,所述活化温度为200-500℃,时间为30-120min。进一步,步骤(3)中,所述过筛为过100-200目筛。本专利技术的有益效果:本专利技术方法工艺简单,其不以木材为原料,而以废弃物山核桃壳为原料,原料来 ...
【技术保护点】
一种活性炭的制备方法,其特征在于,包括如下步骤:(1)以山核桃壳为原料,将山核桃壳破碎后过筛,然后加入到磷酸溶液中浸泡16‑24h,过滤;(2)将过滤得到的滤渣置于马弗炉中加热活化,然后冷却至室温,得到活化物;(3)将活化物酸洗,再水洗至中性,最后过筛,即得;步骤(1)中,所述山核桃壳与磷酸溶液的重量比为1:3‑6。
【技术特征摘要】
1.一种活性炭的制备方法,其特征在于,包括如下步骤:(1)以山核桃壳为原料,将山核桃壳破碎后过筛,然后加入到磷酸溶液中浸泡16-24h,过滤;(2)将过滤得到的滤渣置于马弗炉中加热活化,然后冷却至室温,得到活化物;(3)将活化物酸洗,再水洗至中性,最后过筛,即得;步骤(1)中,所述山核桃壳与磷酸溶液的重量比为1:3-6。2.如权利要求1所述的活性炭的制备方法,其特征在于,...
【专利技术属性】
技术研发人员:叶孙龙,
申请(专利权)人:句容市百诚活性炭有限公司,
类型:发明
国别省市:江苏,32