The invention relates to a nano silver composite collagen medical dressing and a preparation method thereof. This method firstly dialdehyde polysaccharide solution and silver nitrate solution after mixing and boiling reflux, to be mixed liquid cooled to room temperature after dialysis and centrifugation, the supernatant to obtain the nano silver solution, then the collagen sponge soaked in nano silver solution, freeze drying to obtain the nano silver composite collagen dressings. The invention adopts a method of reducing green nano silver solution stable and narrow particle size distribution was obtained, in addition dialdehyde polysaccharide in solution can occur Schiff chemical crosslinking reaction with collagen, so as to enhance the physical properties of collagen sponge. The prepared nano silver composite collagen dressings with broad-spectrum antimicrobial resistance, rapid hemostasis, high mechanical properties, good moisture resistance and biocompatibility characteristics, has potential market application prospect in the treatment of burn and scald area.
【技术实现步骤摘要】
一种纳米银复合胶原医用敷料及其制备方法
本专利技术涉及生物医用材料
，具体而言涉及一种具有广谱抑菌性、快速止血性、良好保湿性和生物相容性特点的且能够促进烧伤、烫伤创面快速愈合的复合胶原医用敷料及其制备方法。
技术介绍
在日常生活中，烧伤和烫伤屡见不鲜。烧伤和烫伤创面容易被致病微生物感染，因此临床上大量使用抗生素、消毒剂和杀菌剂等化学药物来杀灭微生物，进而促进创面快速愈合。其化学药物的大量使用会引起微生物的耐药性，如大肠杆菌对卡那霉素和链霉素的耐药性，伤寒杆菌对氯霉素的耐药性等。由微生物耐药性此引发的全球性微生物灾害事件频频发生，因此研究开发新型低成本、安全性高的杀菌材料迫在眉睫。纳米银(AgNPs)作为无机抗菌材料可以有效地杀灭细菌、真菌和支原体等致病微生物。此外，纳米银的抗菌活性较高且不易引起微生物的耐药性。因此纳米银在用于治疗烧伤和烫伤具有显著的优势。Ag+可以被还原剂还原成Ag0，进而制备得到纳米银。在文献报道的纳米银的制备方法中，肼、N,N-二甲基甲酰胺和硼氢化钠等有毒害的化学试剂常作为还原剂制备得到纳米银，因此该方法制备的纳米银不能用于生物医学材料...
【技术保护点】
一种纳米银复合胶原医用敷料，其特征在于以双醛多糖还原Ag
【技术特征摘要】
1.一种纳米银复合胶原医用敷料，其特征在于以双醛多糖还原Ag+制备纳米银溶液，并将其均匀引入到胶原海绵基质中制备得到纳米银复合胶原医用敷料，其具体制备方法如下：(1)将质量浓度为0.5%~10%的双醛多糖溶液与质量浓度为0.1%~20%的硝酸银溶液共混后在室温下避光搅拌10~30min，之后将混合溶液煮沸、冷凝回流5~60min，待其冷却到室温后透析5天，然后在4000~8000r/min的速度下离心10~20min，取上清液即得纳米银溶液；(2)将胶原溶于去离子水中得到质量浓度为0.3%~0.8%的胶原溶液，之后将其注入模具...
【专利技术属性】
技术研发人员：李德富，葛黎明，穆畅道，史鲁浙，杨森，
申请(专利权)人：四川大学，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。