The invention discloses a method for preparing a solid wood multilayer mirror panel, which comprises the following steps: (1) the use of substrate material: wood of Eucalyptus junctionless, without uneven substrate and substrate, no cracks, no internal splicing overlap; (2) melamine impregnated paper preparation: three melamine resin glue impregnated decorative paper, glue quality printing decorative paper 150% 160%; (3) pressing in steps: (1) the wood substrate surface and the lower surface are affixed to the melamine impregnated paper get pressed blank. The solid wood multilayer mirror panel prepared by the method has the advantages of high bonding strength, good surface impact resistance and difficult deformation.
【技术实现步骤摘要】
一种实木多层镜面板的制备方法
本专利技术属于材料
，具体涉及一种实木多层镜面板的制备方法。
技术介绍
目前市场现有的纯实木家具的表面处理工艺主要有实木贴皮和涂漆两种。就涂漆家具而言，其甲醛释放量多为E2级。目前市场上的实木多层板进行镜面的三聚氰胺浸渍纸饰面厚度偏差大，表面清晰度不高，实木亮度差，极大地限制了实木在高端家具的应用，因此实木多层板只能进行三聚氰胺浸渍纸的浮雕饰面和亚面饰面，主要用于实木家具的侧板、内堂板以及中低端的门板。此外，实木多层板板面易出现碳化、横条、起层等现象，不能用作中高端家具的门板。
技术实现思路
针对上述技术缺陷，本专利技术的目的在于提供一种实木多层镜面板的制备方法，该方法制备得到的实木多层镜面板具有粘结强度高、表面耐冲击性好、不易变形等特点。本专利技术目的是通过如下技术方案实现的：本专利技术实木多层镜面板的制备方法，包括以下步骤：(1)选材：实木基板选用无结的桉木，基材内部无凹凸不平，且基材内部拼接无裂缝、无重叠；(2)三聚氰胺浸渍纸的制备：三聚氰胺树脂胶液浸渍印刷装饰纸，上胶量是印刷装饰纸质量的150％-160％；(3)压贴：在步骤...
【技术保护点】
一种实木多层镜面板的制备方法，其特征在于，包括以下步骤：(1)选材：实木基板选用无结的桉木，基材内部无凹凸不平，且基材内部拼接无裂缝、无重叠；(2)三聚氰胺浸渍纸的制备：三聚氰胺树脂胶液浸渍印刷装饰纸，上胶量是印刷装饰纸质量的150％‑160％；(3)压贴：在步骤(1)所得实木基板上、下表面依次贴三聚氰胺浸渍纸得到压贴组坯；在温度为60～70℃条件下，将压贴组坯送入热压机，第一段为升温段：把温度从70℃升温至140℃、压力设定在13～15MPa进样；第二段为保温段：温度为130～140℃、压力设定在13～15MPa，压贴时间25～35分钟，第三段为降温段：压制完成后，冷却至...
【技术特征摘要】
1.一种实木多层镜面板的制备方法，其特征在于，包括以下步骤：(1)选材：实木基板选用无结的桉木，基材内部无凹凸不平，且基材内部拼接无裂缝、无重叠；(2)三聚氰胺浸渍纸的制备：三聚氰胺树脂胶液浸渍印刷装饰纸，上胶量是印刷装饰纸质量的150％-160％；(3)压贴：在步骤(1)所得实木基板上、下表面依次贴三聚氰胺浸渍纸得到压贴组坯；在温度为60～70℃条件下，将压贴组坯送入热压机，第一段为升温段：把温度从70℃升温至140℃、压力设定在13～15MPa进样；第二段为保温段：温度为130～1...
【专利技术属性】
技术研发人员：潘勇，赵万全，任远军，
申请(专利权)人：成都帝龙新材料有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。