The invention belongs to the field of a processing technology, in particular to a method for improving the stability of wicker color dyeing method, specific methods are as follows: (1) a cleaning and temperature; (2) soaking liquid immersion and drying treatment; dyeing process; (3) the invention of wicker, not only pure, shiny uniform dyeing, with a hint of floral scent, no smell, no toxic residues, mildew proofing effect, and effectively improve the wicker flexibility, improve its quality effectively avoid the willow, broken phenomenon in the process of preparation and follow-up, making more effort, improve work efficiency; dyed after willow not only good wear resistance, wipe will not fade phenomenon will appear with the hands or cloth, dyeing and not just outside structure on the wicker were stained, The color can effectively penetrate into the inside of the wicker and effectively improve the quality of the wicker.
【技术实现步骤摘要】
一种提高柳条上色稳定性的染色方法
本专利技术属于柳条加工
,尤其是一种提高柳条上色稳定性的染色方法。
技术介绍
柳条是一种重要的柳编原材料,柳条具有优良的柔韧性和拉伸强度,十分适合进行柳编,但是柳条不易进行染色,染色后容易褪色,造成制品的颜色单一,或者染色后柳条颜色不均匀,影响柳条编制品的品质,而且极易发霉虫蛀,使得柳条编制品使用寿命大大缩短;因此,专利技术一种能有效解决以上问题的柳条的染色方法是目前亟待解决的问题。
技术实现思路
针对上述问题,本专利技术旨在提供一种提高柳条上色稳定性的染色方法。本专利技术通过以下技术方案实现:一种提高柳条上色稳定性的染色方法,具体方法如下:(1)柳条清洗及变温处理选取粗细均匀、表面光洁的柳条,用温度为43~45℃的温水清洗干净,置入温度为-13~-11℃的冷冻箱内冷冻53~55min,取出,置入温度为51~53℃的烘烤箱内烘烤8~9min,取出,室温自然冷却,得一次柳条;(2)浸泡液浸泡及干燥处理将一次柳条浸没于浸泡液中浸泡36~38min,取出,用功率为320~330W的微波处理13~14min,在温度为43~45℃、相对湿度为17%~19%的条件下风干至水分含量为9%~10%,得二次柳条;所述的浸泡液,由以下重量份的原料制成:酒石酸钾18~19份、尼可刹米3.4~3.6份、水杨酸镁7.7~7.9份、冰醋酸15~16份、硼酸钠12.5~13份、水130~140份;(3)染色处理将二次柳条浸没于肉桂提取液中浸泡17~18min,取出,用光照强度为970~980Lx的红色光照射24~26min,在温度为43~45℃、相对 ...
【技术保护点】
一种提高柳条上色稳定性的染色方法,其特征在于,具体方法如下:(1)柳条清洗及变温处理选取粗细均匀、表面光洁的柳条,用温度为43~45℃的温水清洗干净,置入温度为‑13~‑11℃的冷冻箱内冷冻53~55min,取出,置入温度为51~53℃的烘烤箱内烘烤8~9min,取出,室温自然冷却,得一次柳条;(2)浸泡液浸泡及干燥处理将一次柳条浸没于浸泡液中浸泡36~38min,取出,用功率为320~330W的微波处理13~14min,在温度为43~45℃、相对湿度为17%~19%的条件下风干至水分含量为9%~10%,得二次柳条;所述的浸泡液,由以下重量份的原料制成:酒石酸钾18~19份、尼可刹米3.4~3.6份、水杨酸镁7.7~7.9份、冰醋酸15~16份、硼酸钠12.5~13份、水130~140份;(3)染色处理将二次柳条浸没于肉桂提取液中浸泡17~18min,取出,用光照强度为970~980Lx的红色光照射24~26min,在温度为43~45℃、相对湿度为17%~19%的条件下风干至水分含量为9%~10%,浸没于染色剂中浸泡15~16h,取出,用光照强度为1100~1200Lx的黄色光照射93 ...
【技术特征摘要】
1.一种提高柳条上色稳定性的染色方法,其特征在于,具体方法如下:(1)柳条清洗及变温处理选取粗细均匀、表面光洁的柳条,用温度为43~45℃的温水清洗干净,置入温度为-13~-11℃的冷冻箱内冷冻53~55min,取出,置入温度为51~53℃的烘烤箱内烘烤8~9min,取出,室温自然冷却,得一次柳条;(2)浸泡液浸泡及干燥处理将一次柳条浸没于浸泡液中浸泡36~38min,取出,用功率为320~330W的微波处理13~14min,在温度为43~45℃、相对湿度为17%~19%的条件下风干至水分含量为9%~10%,得二次柳条;所述的浸泡液,由以下重量份的原料制成:酒石酸钾18~19份、尼可刹米3.4~3.6份、水杨酸镁7.7~7.9份、冰醋酸15~16份、硼酸钠12.5~13份、水130~140份;(3)染色处理将二次柳条浸没于肉桂提取液中浸泡17~18min,取出,用光照强度为970~980Lx的红色光照射24~26min,在温度为43~45℃、相对湿度为17%~19%的条件下风干至水分含量为9%~10%,浸没于染色剂中浸泡15~16h,取出,用光照强度为1100~1200Lx的黄色光照射93~95min,置入温度为47~49℃的烘烤箱内烘烤13~14min,取出,在温度为28~30℃、相对湿度为17%~19%的条件下自然风干;所述的染色剂,由以下重量份的原料制成:马齿苋13~14份、薄荷叶8~9份、扫帚菜22~23份、桑叶15~16份、桃叶6.5~7份...
【专利技术属性】
技术研发人员:徐学进,
申请(专利权)人:阜南佳利工艺品有限公司,
类型:发明
国别省市:安徽,34