The present invention relates to the technical field of automobile paint, belonging to an oxidation resistant paint special type truck bumper, the oxidation resistance type truck bumper by special paint alkyd resin, titanium dioxide, violet, blue, amino resin, dispersing agent, defoaming agent, leveling agent and antioxidant according to the weight ratio of 90 to 110:1 ~ 3:0.3 ~ 0.8:1 ~ 2:50 ~ 70:12 ~ 18:12 ~ 18:12 ~ 18:0.1 ~ 0.6. The invention overcomes the defects of the existing technology, which consists of 168 phenolic antioxidants antioxidants and antioxidant, antioxidant 168 compounded with phenol antioxidant compound, and peroxides, phosphate oxide stable, not only prevent a chain reaction, but also improve the stability of polymer to light, heat and oxygen efficiency excellent, can effectively reduce oxidative discoloration of paint.
【技术实现步骤摘要】
一种耐氧化型卡车保险杠专用油漆
本专利技术涉及汽车油漆
，具体属于一种耐氧化型卡车保险杠专用油漆。
技术介绍
塑料保险杠是由外板、缓冲材料和横梁等三部分组成。其中外板和缓冲材料用塑料制成，横梁用厚度为1.5毫米左右的冷轧薄板冲压而成U型槽；外板和缓冲材料附着在横梁上，横梁与车架纵梁螺丝联接，可以随时拆卸下来。这种塑料保险杠使用的塑料，大体上使用聚脂系和聚丙烯系两种材料，采用注射成型法制成。注塑完毕后还需要进行表面处理、喷漆和烘烤，由于汽车99%工作环境均为室外，因此汽车上采用的油漆相对来说比普通的油漆要求要高，否则经过一段时间的日晒雨淋后很容易变色。
技术实现思路
本专利技术的目的是提供了一种耐氧化型卡车保险杠专用油漆，克服了现有技术的不足，耐氧化型卡车保险杠专用油漆由醇酸树脂、钛白粉、永固紫、酞青蓝、氨基树脂、分散剂、消泡剂、流平剂和抗氧化剂组成，其中抗氧化剂由抗氧化剂168和酚类主抗氧剂复合而成，抗氧化剂168与酚类主抗氧剂复合使用，与过氧化物反应，生成氧化性稳定的磷酸酯，不仅阻止了氧化反应的链增值，还能提高聚合物对光的稳定性，抗热氧效能卓越，可以有效的减缓...
【技术保护点】
一种耐氧化型卡车保险杠专用油漆，其特征在于，所述的耐氧化型卡车保险杠专用油漆由醇酸树脂、钛白粉、永固紫、酞青蓝、氨基树脂、分散剂、消泡剂、流平剂和抗氧化剂按照重量比90～110：1～3：0.3～0.8：1～2：50～70：12～18：12～18：12～18：0.1～0.6组成；所述的抗氧化剂由抗氧化剂168和酚类主抗氧剂按照重量比1：1～3组成。
【技术特征摘要】
1.一种耐氧化型卡车保险杠专用油漆，其特征在于，所述的耐氧化型卡车保险杠专用油漆由醇酸树脂、钛白粉、永固紫、酞青蓝、氨基树脂、分散剂、消泡剂、流平剂和抗氧化剂按照重量比90～110：1～3：0.3～0.8：1～2：50～70：12～18：12～18：12～18：0.1～0.6组成；所述的抗氧化剂由抗氧化剂168和酚类主抗氧剂按照重量比1：1～3组成。2.根据权利要求1所述的一种耐氧化型卡车保险杠专用油漆，其特征在于：所述的耐氧化型卡车保险杠专用油漆由醇酸树脂、钛白粉、永固紫、酞青蓝、氨基树脂、分散剂、消泡剂、流平剂和抗氧化剂按照重量比100：1.5：0.5：1.5：60：15：15：15：0.35组成。3.根据权利要求1所述的一...
【专利技术属性】
技术研发人员：查国东，储振亚，储亮，李云雷，
申请(专利权)人：安徽科瑞特模塑有限公司，
类型：发明
国别省市：安徽,34