The invention provides a plate fin heat exchanger corrosion resistant coating and preparation, including the following parts: quality made of waterborne polyurethane acrylate 80 100, 25 40, 20 water glass 25, sodium gluconate 8 12 copies, 5 copies of the 2 disodium EDTA, 8 hydroxy quinoline sulfate 3 6, 2 4 hydroxypropyl methyl cellulose, hydroxypropyl starch 0.4 1, twelve alkyl two methyl ammonium hydroxide 1 3, two 0.1 0.3 azo isobutyronitrile, coating prepared in the invention has excellent resistance to corrosion and rust, dirt resistance. The paint has good leveling, and metal adhesion, corrosion resistance improved significantly, effectively extending the service life of plate fin heat exchanger.
【技术实现步骤摘要】
板翅式换热器防腐耐污涂层及其制备
本专利技术涉及换热器防护涂层
，具体涉及一种板翅式换热器防腐耐污涂层及其制备。
技术介绍
板翅式换热器通常由隔板、翅片、封条、导流片组成。在相邻两隔板间放置翅片、导流片以及封条组成一夹层，称为通道，将这样的夹层根据流体的不同方式叠置起来，钎焊成一整体便组成板束，板束是板翅式换热器的核心，配以必要的封头、接管、支撑等就组成了板翅式换热器。板翅式换热器换热效率高，适应性强，可适用于：气－气、气－液、液－液、各种流体之间的换热以及发生集态变化的相变换热，通过流道的布置和组合能够适应：逆流、错流、多股流、多程流等不同的换热工况，但板翅式换热器容易堵塞，不耐腐蚀，在使用过程中常常需要清洗维护，使用寿命短，且极大的限制的使用环境。现有技术中为提高板翅式换热器的工作效率和寿命常对其涂覆表面防护涂层。
技术实现思路
针对上述存在的问题，本专利技术提出了一种板翅式换热器防腐耐污涂层及其制备，制得的涂层具有优异的防腐防锈、耐水耐污性能，且涂层流平性好，与金属结合力强，缓蚀性显著提高，有效延长了板翅式换热器的使用寿命。为了实现上述的目的，本专利技术采...
【技术保护点】
板翅式换热器防腐耐污涂层，其特征在于，包括以下质量份数制成：水性聚氨酯80‑100份、丙烯酸酯25‑40份、水玻璃20‑25份、葡萄糖酸钠8‑12份、乙二胺四乙酸钠盐2‑5份、8‑羟基喹啉硫酸盐3‑6份、羟丙基甲基纤维素2‑4份、羟丙基淀粉0.4‑1份、十二烷基二甲基氧化铵1‑3份、偶氮二异丁腈0.1‑0.3份。
【技术特征摘要】
1.板翅式换热器防腐耐污涂层，其特征在于，包括以下质量份数制成：水性聚氨酯80-100份、丙烯酸酯25-40份、水玻璃20-25份、葡萄糖酸钠8-12份、乙二胺四乙酸钠盐2-5份、8-羟基喹啉硫酸盐3-6份、羟丙基甲基纤维素2-4份、羟丙基淀粉0.4-1份、十二烷基二甲基氧化铵1-3份、偶氮二异丁腈0.1-0.3份。2.根据权利要求1所述的板翅式换热器防腐耐污涂层，其特征在于，包括以下质量份数制成：水性聚氨酯90-100份、丙烯酸酯30-40份、水玻璃22-25份、葡萄糖酸钠10-12份、乙二胺四乙酸钠盐4-5份、8-羟基喹啉硫酸盐5-6份、羟丙基甲基纤维素3-4份、羟丙基淀粉0.8-1份、十二烷基二甲基氧化铵2-3份、偶氮二异丁腈0.2-0.3份。3.根据权利要求1或2所述的板翅式换热器防腐耐污涂层，其特征在于：所述8-羟基喹啉硫酸盐为摩尔比1:3:2的镁盐、锂盐、铝盐的混合物。4.根据权利要求1或2所述的板翅式换热器防腐耐污涂层的制...
【专利技术属性】
技术研发人员：张凌霞，
申请(专利权)人：安徽普瑞普勒传热技术有限公司，
类型：发明
国别省市：安徽,34