The invention discloses a 2,2,6,6 four methyl preparation method of 4 piperidinyl stearic acid. The method using stearic acid as the starting material, first in sulfuric acid with methanol catalyzed esterification reaction preparation of intermediate methyl stearate, using p-toluene sulfonic acid as catalyst, and 2,2,6,6 four methyl 4 piperidine alcohol ester was prepared by 2,2,6,6 piperidinyl four methyl stearate. The invention has the advantages of easy availability of raw and auxiliary materials, mild reaction conditions, simple and safe operation, high conversion rate, stable product quality, cleanness and environmental protection.
【技术实现步骤摘要】
2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法
：本专利技术涉及高分子添加剂的制备方法，具体涉及一种光稳定剂2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法。
技术介绍
：2,2,6,6-四甲基-4-哌啶基硬脂酸酯是一种新型的受阻胺光稳定剂，具有位阻效应、能有效分解过氧化物、基发态氧，捕捉游离基等；有效基团具有再生功能；提供给塑料优异的表面性质的保护；高溶解性/与聚烯烃和苯乙烯等相容性；与其他稳定剂，特别是高分子量的受阻胺光稳定剂有最佳协同作用。
技术实现思路
：本专利技术的目的是为了克服以上的不足，提供一种2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法，原辅材料易得，反应条件温和，操作安全简便，转化率高，产品质量稳定。本专利技术是通过以下技术方案来实现：一种2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法，以硬脂酸为起始原料，先在硫酸催化下与甲醇反应制备甲酯化中间体硬脂酸甲酯,再采用对甲苯磺酸为催化剂，与2,2,6,6-四甲基-4-哌啶醇进行酯交换制备2,2,6,6-四甲基哌啶基硬脂酸酯。本专利技术的进一步改进在于：合成路线如下：本专利技术的进一...
【技术保护点】
一种2,2,6,6‑四甲基‑4‑哌啶基硬脂酸酯的制备方法，其特征是：以硬脂酸为起始原料，先在硫酸催化下与甲醇反应制备甲酯化中间体硬脂酸甲酯,再采用对甲苯磺酸为催化剂，与2,2,6,6‑四甲基‑4‑哌啶醇进行酯交换制备2,2,6,6‑四甲基哌啶基硬脂酸酯。
【技术特征摘要】
1.一种2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法，其特征是：以硬脂酸为起始原料，先在硫酸催化下与甲醇反应制备甲酯化中间体硬脂酸甲酯,再采用对甲苯磺酸为催化剂，与2,2,6,6-四甲基-4-哌啶醇进行酯交换制备2,2,6,6-四甲基哌啶基硬脂酸酯。2.根据权利要求1所述一种2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法，其特征是：所述合成路线如下：3.根据权利要求1所述一种2,2,6,6-四甲基-4-哌啶基硬脂酸酯的制备方法，其特征是：所述制备方法的具体步骤如下：A、甲酯化：在甲醇中投入硬脂酸，再加入硫酸，升温回流3h，取样作反应终点判断，合格后，常压蒸馏脱去甲醇，温度≤90℃，最后于60～65℃加水洗涤两次，得硬脂酸甲酯；B、酯交换：在甲苯中投入硬脂酸甲酯，用氮气置换掉空气，升温蒸出甲苯，蒸完后通氮降温至25～30℃，投入2,2,6,6-四甲基-4-哌啶醇，氮气保护下控制温度于112～116℃滴加对甲苯磺酸甲苯溶液...