The invention provides a method for producing / low density fiber board and its products, the production steps are as follows: a) of wood fiber after separation, screening, electric heating, steam injection, grinding chamber body made by hot mill fiber; b) hot mill chamber output fiber by spraying pipeline output; c) ecological glue isocyanate adhesive through sizing of screw pump, the pump into the drying pipe at the entrance, through high pressure nozzle, and is dry fiber mixed and uniform, and then continue to dry in the dry pipe; d) the sizing process after the fiber was pressed on the hot press; the steps of B) and C) is at the same time; the steps of a) to the raw materials by hot mill fiber processing application rate was 700 820kg/m
【技术实现步骤摘要】
一种中/高密度纤维板的生产方法
本专利技术属于纤维板生产
，涉及一种中/高密度纤维板的生产方法。
技术介绍
普通的密度板制作过程中通常会使用脲醛胶，而脲醛胶是一种甲醛化合物，所以密度板天生就含有甲醛。目前在国际上，按照甲醛释放量等级被分为E2、E1、E0、NAF(未添加甲醛胶)四个级别，即E2≤30mg/100g,E1≤9mg/100g(欧盟8mg/100g)、E0≤3mg/100g、NAF≤0.06ppm(约0.5mg/100g)，NAF级别是每100g板材样品里含甲醛的量小于或等于0.5mg/100g。然而，目前世界上只有芬兰、日本、美国等少数国家执行NAF级标准，国内还没有未添加甲醛胶粘剂即NAF级产品标准出台。而且，NAF级别高标准板材的生产，对厂家的生产技术要求非常高，而且生产成本高，消耗大。
技术实现思路
本专利技术的目的在于为了克服现有生产技术的上述缺点，提供一种中/高密度纤维板的生产方法，本专利技术采用的技术方案为：一种中/高密度纤维板的生产方法，其生产步骤如下：a)将木质纤维分离后，进行水洗、电加热喷蒸，经热磨机磨室体处理制成纤维；b)所述热磨...
【技术保护点】
一种中/高密度纤维板的生产方法，其生产步骤如下：a)将木质纤维分离后，进行筛选，电加热喷蒸，经热磨机磨室体处理制成纤维；b)所述热磨机磨室体产出的纤维，产出至与热磨机相连的喷放管道；c)将生态胶异氰酸酯胶通过施胶螺杆泵泵入喷放管道内的入口处，胶粘剂经高压喷嘴喷洒在纤维上，与所述产出的纤维进行混合并均匀；d)所述纤维与所述胶粘剂混合均匀后进入干燥管道内进行干燥；e)干燥后，将施胶处理后的纤维再经热压机上进行热压；所述步骤a)要经热磨机加工的原纤维材料施加量为700‑820kg/m
【技术特征摘要】
1.一种中/高密度纤维板的生产方法，其生产步骤如下：a)将木质纤维分离后，进行筛选，电加热喷蒸，经热磨机磨室体处理制成纤维；b)所述热磨机磨室体产出的纤维，产出至与热磨机相连的喷放管道；c)将生态胶异氰酸酯胶通过施胶螺杆泵泵入喷放管道内的入口处，胶粘剂经高压喷嘴喷洒在纤维上，与所述产出的纤维进行混合并均匀；d)所述纤维与所述胶粘剂混合均匀后进入干燥管道内进行干燥；e)干燥后，将施胶处理后的纤维再经热压机上进行热压；所述步骤a)...