The invention provides a production method without adding high density fiberboard formaldehyde adhesive, its production steps are as follows: a) of wood fiber after separation, screening, cooking, grinding chamber body made by hot mill fiber; b) hot mill chamber output fiber by blowline output; c) will not add formaldehyde adhesive MDI sizing by screw pump, pump into the drying pipe at the entrance of MDI adhesive by high pressure nozzle, and the output of the fiber was mixed and uniform; d) of the fiber and the adhesive in the mixing and drying in the drying pipe; e after drying, the sizing) treated fiber was pressed on the hot press. The invention solves the problem that the production of MDI glue fiber board products is easy to plug.
【技术实现步骤摘要】
一种未添加甲醛胶粘剂中/高密度纤维板的生产方法
本专利技术属于纤维板生产
，涉及一种未添加甲醛胶粘剂中/高密度纤维板的生产方法。
技术介绍
传统的施胶技术采用的是管道喷胶，即从热磨机磨室体刚出来的纤维与胶粘剂均匀混合后进入干燥管道进行干燥。过程主要是通过齿轮泵将胶粘剂泵入热磨机出口的纤维喷放管道，经高压喷嘴将胶粘剂均匀喷散在纤维表面，达到均匀施胶的目的。然而现有的这种生产技术，由于刚从热磨机喷出的纤维含水率高，容易蒸发至胶管而造成胶管的堵塞，使得部分纤维难以与胶接触，以致施胶不均匀，影响板材产品强度。
技术实现思路
本专利技术的目的在于为了克服现有生产技术的上述缺点，提供一种未添加甲醛胶粘剂中/高密度纤维板的生产方法，本专利技术采用的技术方案为：一种未添加甲醛胶粘剂中/高密度纤维板的生产方法，其生产步骤如下：a)将木质纤维分离后，进行筛选、蒸煮，经热磨机磨室体处理制成纤维；b)将热磨机磨室体产出的纤维经喷放管道产出至干燥管道；c)将未添加甲醛的胶粘剂MDI通过施胶螺杆泵，泵入干燥管道内的入口处，MDI胶粘剂经高压喷嘴喷出，与所述产出的纤维进行混合并均匀；d)所述...
【技术保护点】
一种未添加甲醛胶粘剂中/高密度纤维板的生产方法，其生产步骤如下：a)将木质纤维分离后，进行筛选、蒸煮，经热磨机磨室体处理制成纤维；b)将热磨机磨室体产出的纤维经喷放管道产出至干燥管道；c)将未添加甲醛的胶粘剂MDI通过施胶螺杆泵，泵入干燥管道内的入口处，MDI胶粘剂经高压喷嘴喷出，与所述产出的纤维进行混合并均匀；d)所述纤维与所述胶粘剂在混合均匀的同时，在干燥管道内进行干燥；e)干燥后，将施胶处理后的纤维在热压机上进行热压。
【技术特征摘要】
1.一种未添加甲醛胶粘剂中/高密度纤维板的生产方法，其生产步骤如下：a)将木质纤维分离后，进行筛选、蒸煮，经热磨机磨室体处理制成纤维；b)将热磨机磨室体产出的纤维经喷放管道产出至干燥管道；c)将未添加甲醛的胶粘剂MDI通过施胶螺杆泵，泵入干燥管道内的入口处，MDI胶粘剂经高压喷嘴喷出，与所述产出的纤维进行混合并均匀；d)所述纤维与所述胶粘剂在混合均匀的同时，在干燥管道内进行干燥；e)干燥后，将施胶处理后的纤维在热压机上进行热压。2.根据权利要求1所述的纤维板的生产方法...