The invention discloses a method for treating hemorrhoids material preparation process, the tourmaline powder, graphite, deionized water and sodium silicate mixed mixed solution, PVA solution is added into the mixture, the PVA solution and the mixed solution of a step fully in the mixed slurry; the slurry evenly soaked in sizing the cloth, and then dried to obtain the final cloth. The invention of tourmaline and graphene by physical methods, the graphene composite in tourmaline stone molecules, the tourmaline radiation such as far infrared ray intensity has been significantly improved, at the same time, in the process of cloth, then the graphene covered by tourmaline pulping treatment of slurry, fully impregnated, penetrate into cotton go. Make an organic and solid combination of the two. A dry treated cloth that is washable and abrasion resistant and allows the fabric to heal for long periods without impairment.
【技术实现步骤摘要】
一种用于治疗痔疮的布料制备工艺
本专利技术涉及布料制备工艺领域，具体的，涉及一种用于治疗痔疮的布料制备工艺。
技术介绍
目前市场上虽然布料种类繁多，然而并没有存在具有治疗痔疮功效的布料。众所周知，任何人一旦患上了痔疮，它给患者带来的难以启齿的痛苦，一辈子都甩不掉，吃药、敷药、针灸、切割，都只能解决短暂的痛苦，久之必然复发。基于上述原因，有必要设计一种用于治疗痔疮的布料的制备工艺，以用于得到上述布料，从而用于缓解生活中痔疮患者的痛苦。
技术实现思路
针对现有技术中存在的不足，本专利技术提供了一种用于治疗痔疮的布料制备工艺。本专利技术是通过如下技术方案实现的：一种用于治疗痔疮的布料制备工艺，包括如下步骤：1）配置原材料A，其包括如下步骤：a)将托玛琳粉、石墨烯、去离子水和硅酸钠混合得到混合溶液；b)在上述混合料中加入PVA溶液，使得PVA溶液与步骤a中的混合溶液充分混合；2）将原材料A制作的浆料均匀浸渍上浆在布料上面，然后干燥处理。上述技术方案中，原材料A中各组分具有如下质量份数比：托玛琳粉5~30、PVA溶液2~10、去离子水180~200、石墨烯0.5~2、硅酸纳0....
【技术保护点】
一种用于治疗痔疮的布料制备工艺，包括如下步骤： 1）配置原材料A，其包括如下步骤：a)将托玛琳粉、石墨烯、去离子水和硅酸钠混合得到混合溶液；b)在上述混合料中加入PVA溶液，使得PVA溶液与步骤a中的混合溶液充分混合；2）将原材料A制作的浆料均匀浸渍上浆在布料上面，然后干燥处理。
【技术特征摘要】
1.一种用于治疗痔疮的布料制备工艺，包括如下步骤：1）配置原材料A，其包括如下步骤：a)将托玛琳粉、石墨烯、去离子水和硅酸钠混合得到混合溶液；b)在上述混合料中加入PVA溶液，使得PVA溶液与步骤a中的混合溶液充分混合；2）将原材料A制作的浆料均匀浸渍上浆在布料上面，然后干燥处理。2.如权利要求1所述的一种用于治疗痔疮的布料制备工艺，其特征在于：原材料A中各组分具有如下质量份数比：托玛琳粉5~30、PVA溶液2~10、去离子水180~...