一种退镀层清洗剂及其制备方法技术

本发明专利技术公开了一种退镀层清洗剂，是由按照重量份计的以下原料制备得到的：六亚甲基四胺65‑75份、硝酸3‑5份、盐酸14‑16份、聚乙烯醇3‑6份、硫酸钠8‑10份、氯化钙12‑14份、磷酸6‑8份、水20‑24份；并提供了其制备方法。本发明专利技术的有益效果为：本发明专利技术提供的一种退镀层清洗剂及其制备方法，能够快速、彻底的退除物件表面的镀层，同时，还可对物件表面进行无损伤抛光，为再次镀层奠定了良好基础。

Coating cleaning agent and preparation method thereof

The invention discloses a back coating cleaning agent is composed of the following raw materials according to weight prepared: six four methylene amine 65 75 copies, 5 copies, 3 nitrate hydrochloride 14 16 copies, 6 copies, 3 polyvinyl alcohol sodium sulfate and calcium chloride 8 10 12 14 a 6, phosphate 8 and water 20 24; and provides a method for preparing them. The beneficial effect of the invention is: a back coating cleaning agent and preparation method thereof provided by the invention can quickly and thoroughly remove the coating on the surface of the object, at the same time, but also on the surface of the object without polishing damage, laid a good foundation for re coating.

【技术实现步骤摘要】
一种退镀层清洗剂及其制备方法
本专利技术涉及化学制剂领域，具体涉及一种退镀层清洗剂及其制备方法。
技术介绍
在工业或民用上使用的用来除去污垢的化学或生物制剂统称为清洗剂。退镀层，是将电镀或化学镀的物件上的镀层清除掉，以便于再次镀层，先退镀层是为了防止镀层的厚度不均一造成镀层脱落。但现有的市售产品大多退镀层速度慢且无法彻底退除。
技术实现思路
本专利技术的目的就是针对上述现有技术中的缺陷，提供了一种退镀层清洗剂及其制备方法。为了实现上述目的，本专利技术提供的技术方案为：一种退镀层清洗剂，是由按照重量份计的以下原料制备得到的：六亚甲基四胺65-75份、硝酸3-5份、盐酸14-16份、聚乙烯醇3-6份、硫酸钠8-10份、氯化钙12-14份、磷酸6-8份、水20-24份。进一步的，上述的一种退镀层清洗剂，是由按照重量份计的以下原料制备得到的：六亚甲基四胺68份、硝酸4份、盐酸15份、聚乙烯醇5份、硫酸钠8份、氯化钙12份、磷酸8份、水23份。进一步的，上述的一种退镀层清洗剂，所述清洗剂是将除水以外的各组分置于水浴70℃环境下，边搅拌边加入水，待其完全搅拌均匀后，再保持水浴加热2h后，制备得到的。本文档来自技高网...

【技术保护点】
一种退镀层清洗剂，其特征在于，是由按照重量份计的以下原料制备得到的：六亚甲基四胺65‑75份、硝酸3‑5份、盐酸14‑16份、聚乙烯醇3‑6份、硫酸钠8‑10份、氯化钙12‑14份、磷酸6‑8份、水20‑24份。

【技术特征摘要】
1.一种退镀层清洗剂，其特征在于，是由按照重量份计的以下原料制备得到的：六亚甲基四胺65-75份、硝酸3-5份、盐酸14-16份、聚乙烯醇3-6份、硫酸钠8-10份、氯化钙12-14份、磷酸6-8份、水20-24份。2.根据权利要求1所述的一种退镀层清洗剂，其特征在于，是由按照重量份计的以下原料制备得到的：六亚甲基四胺68份、硝酸4份、盐酸15份、聚乙烯醇5份、硫酸钠8份、氯化钙12份、...

【专利技术属性】
技术研发人员：银柳香，
申请(专利权)人：柳州立洁科技有限公司，
类型：发明
国别省市：广西,45