The invention discloses a Ti12LC titanium alloy strengthening and Toughening Heat treatment process of Ti12LC titanium alloy strengthening and Toughening Heat treatment process comprises the following steps: S1: first stage solution; S2: S3: second stage cold furnace; solid solution; aging treatment: S4. The Ti12LC titanium alloy strengthening and Toughening Heat treatment benefits are as follows: 1, using piecewise heat treatment method of solid solution and aging, which can be obtained by 5 to 30% primary equiaxed alpha phase and 10 ~ 20% secondary phase and lamellar laths or fine acicular transformed beta tissue composed of duplex microstructure, 2, through temperature control the two stages of solution can adjust the volume fraction of primary equiaxed alpha phase and secondary phase lath, thereby regulating the strength and ductility of Ti12LC alloy, and improve its strength and toughness, 3 of the invention, the heat treatment process is simple and feasible, excellent product performance, uniform structure, and is suitable for large-scale industrial production.
【技术实现步骤摘要】
一种Ti12LC钛合金的强韧化热处理工艺
本专利技术涉及一种热处理工艺，尤其涉及Ti12LC钛合金的强韧化热处理工艺。
技术介绍
钛及钛合金由于具有比强度高、无磁性、热膨胀系数低、耐腐蚀、中温性能好等一系列优点，作为一种重要的金属结构材料，不仅被大量应用于航空航天工业及海洋化工工业，而且作为汽车用材很早就引起人们的重视。然而钛合金的制造成本相对于钢铁、铝合金等大量使用的传统金属材料而言要高出许多，较高的成本在一定程度上阻碍了其在民用领域的应用。因此如何降低钛合金材料的成本成为材料科学工作者研究的热点和重点。Ti12LC合金是西北有色金属研究院自行研制采用廉价中间合金Mo-Fe所设计的低成本钛合金，其性能与TC11钛合金相当，成本可降低10％以上。常规的Ti12LC合金热处理工艺为：固溶处理(β转变温度Tβ以下40～100℃保温60～120min后空冷)+时效处理(480～600℃保温6～10h空冷到室温)。经上述热处理工艺处理的Ti12LC合金性能基本满足航空航天常用钛合金的性能需求，但是其微观组织均匀性较差，性能可调控空间小，强度与塑韧性匹配不佳，对于更大规格、...
【技术保护点】
一种Ti12LC钛合金的强韧化热处理工艺，其特征在于，Ti12LC钛合金的强韧化热处理工艺包括以下步骤：S1:第一阶段固溶，将Ti12LC合金锻件放入炉中，升温到β转变温度T
【技术特征摘要】
1.一种Ti12LC钛合金的强韧化热处理工艺，其特征在于，Ti12LC钛合金的强韧化热处理工艺包括以下步骤：S1:第一阶段固溶，将Ti12LC合金锻件放入炉中，升温到β转变温度Tβ以下10～30℃，保温60～120min；S2：炉冷，关闭电阻炉，使锻件随炉冷却至β转变温度Tβ以下60～100℃；S3：第二阶段固溶，Ti12LC合金锻件在β转变温度Tβ以下60～100℃进行保温，保温60～120min，然后...
【专利技术属性】
技术研发人员：万家荣，
申请(专利权)人：天津皕劼同创精密钛铸造有限公司，
类型：发明
国别省市：天津,12