The invention discloses a novel medium high plastic marine titanium alloy, the titanium alloy with sponge titanium, aluminum, vanadium molybdenum aluminum intermediate alloy, pure metal as raw material preparation, its components and weight percentage: Ti 90.25%-93.0%, Al 2.5% ~ 3%, 2% ~ 2.75% Mo Zr, 2% ~ 3%, 0.5% ~ 1% V. In the method of the invention, through reasonable design of components in the alloy, by controlling the composition of alloy, the optimization of the processing properties of the alloy and improve the rate of finished products, corrosion resistance of Ti31 alloy, Ti75 alloy is obviously improved, and the preparation process is simple and feasible, and good quality products, high pass rate, suitable for large-scale industrial production.
【技术实现步骤摘要】
一种新型中强高塑性船用钛合金及其制备工艺
本专利技术属于钛合金材料制备
，具体涉及一种新型中强高塑性船用钛合金及其制备工艺。
技术介绍
我国已初步建立了船用钛合金的体系。创新研制了不同强度级别的船用合金，也制备出不同规格的管、板、棒、丝材等，已基本能够满足我国工程的需求。中强钛合金由于其强度与塑性的综合性能匹配最适于海洋服役环境应用，因此受到我国船舶行业的重视。目前我国应用最广泛的中强高塑钛合金有TA24(Ti75)合金和TA22(Ti31)合金。Ti75合金是630MPa级的中强高韧性耐蚀钛合金，适用于制造形状复杂的板材冲压并焊接的零部件，在动力装置结构、船舶焊接结构件中获得广泛应用。Ti31合金具有中强高塑、可焊和良好冷加工性能，可以用作声纳导流罩，但目前仍处于研究阶段。虽然现阶段Ti75合金已经得到广泛应用，但生产过程中由于强度、塑性不足的情况，容易导致管材等成形困难，容易开裂等加工问题，因此需要更高的强度和塑性匹配的船用钛合金，以期获得更好地加工性能及使用性能。通过优化合金元素配比一直以来都是优化合金性能的重要手段，在新材料研发过程中取得的成果显著。...
【技术保护点】
一种新型中强高塑性船用钛合金，其特征在于，所述钛合金以海绵钛、铝钼、铝钒中间合金、纯金属为原料制备，其构成组分及其重量百分数分别为：Ti 90.25％～93.0％、Al 2.5％～3.0％、Mo 2.0％～2.75％、Zr 2.0％～3.0％、V 0.5％～1.0％。
【技术特征摘要】
1.一种新型中强高塑性船用钛合金，其特征在于，所述钛合金以海绵钛、铝钼、铝钒中间合金、纯金属为原料制备，其构成组分及其重量百分数分别为：Ti90.25％～93.0％、Al2.5％～3.0％、Mo2.0％～2.75％、Zr2.0％～3.0％、V0.5％～1.0％。2.一种权利要求1所述的新型中强高塑性船用钛合金的制备工艺，其特征在于，包括以下步骤：S1、将海绵钛与合金元素混合均匀后压制自耗电极，再进行3-5次真空自耗电弧熔炼制成规格为Φ150mm的100kg的钛合金铸锭；将铸锭进行3火次开坯锻造，第一次开坯锻造的始锻温度为1150℃，锻造比为5.6，第二火次开坯锻造的始锻温度为1050℃，锻造比为8.4，第三火次开坯...
【专利技术属性】
技术研发人员：万家荣，
申请(专利权)人：天津皕劼同创精密钛铸造有限公司，
类型：发明
国别省市：天津,12