一种轨道用铝合金制造技术

本发明专利技术公开了一种轨道用铝合金，包括以下重量百份比的成分组成：Mg 0.6％～2％；Si 1.2％～6％；Cu 0.8％～3％；Fe 0.05％～0.3％；Mn 0.2％～0.65％；Ti 0.05％～0.1％；Zn 0.1％～0.3％；Ni 0.2％～0.4％；余量为Al和少量杂质。本发明专利技术配方合理，所制作出的铝合金具有高强度、高韧性的特点，同时，重量轻，耐腐蚀性能，具有很好的导热性能，而且拉深强度高，抗冲击性好，具有很高的力学特性，克服了容易开裂，有效地提高了使用寿命。

Aluminum alloy for track

The invention discloses a Aluminum Alloy track, including the following weight percentage composition: Mg 0.6% ~ 2%; Si 1.2% ~ 6%; Cu 0.8% ~ 3%; Fe 0.05% ~ 0.3%; Mn 0.2% ~ 0.65%; Ti 0.05% ~ 0.1%; Zn 0.1% ~ 0.3% Ni; 0.2% ~ 0.4%; the rest is Al and a small amount of impurities. The invention has reasonable formula, produced by the Aluminum Alloy has high strength and high toughness characteristics, at the same time, light weight, corrosion resistance, has good thermal conductivity, and high tensile strength, good impact resistance, has high mechanical properties, overcomes the defects of easy to crack, and effectively improve the use of life.

【技术实现步骤摘要】
一种轨道用铝合金
本专利技术涉及铝合金
，具体涉及一种轨道用铝合金。
技术介绍
铝是产量仅次于钢铁的第二大类金属材料，由于性能好，用途广，需量大，且回收成本低，被誉为“万能金属”。统计表明：我国现有124个产业中有113个行业使用铝制品，产业关联度高达91％，因而铝产业是国民经济持续发展的重要支柱性原材料产业之一。目前，铝合金是轨道交通部件生产厂商广泛采用的铝合金材料，而国内生产的铝合金因其阳极氧化膜均匀性和致密性差，难以满足使用要求，主要表现为部件经过表面处理后，氧化膜致密性和均匀性差，使用过程中很快出现大面积腐蚀而报废。该合金的进口又需要很长的周期，严重制约了我国轨道交通行业的发展。因此，开发满足现实要求铝合金需求迫切。因此，针上述问题，本专利技术提出一种新的方案。
技术实现思路
本专利技术的目的是提供一种重量轻、耐腐蚀性能强，使用寿命长的轨道用铝合金。本专利技术是通过以下技术方案来实现的：一种轨道用铝合金，包括以下重量百份比的成分组成：余量为Al和少量杂质。进一步地，还包括以下重量百分比含量的下列成分：进一步地，所述铝合金通过热挤压成形。本专利技术的有益效果是：本专利技术配方本文档来自技高网...

【技术保护点】
一种轨道用铝合金，其特征在于：包括以下重量百份比的成分组成：

【技术特征摘要】
1.一种轨道用铝合金，其特征在于：包括以下重量百份比的成分组成：余量为Al和少量杂质。2.根据权利要求1所述一种轨道用铝合金，...