The invention discloses a metatitanic acid modified cellulose and preparation method thereof, prepared by the following method: take the bark through cleaning, drying and pulverization after added to n-hexane dewaxing filtration, heating and stirring, washing and drying; the dewaxed product with sodium hydroxide solution at room temperature in a stirred, filtered, in turn with ultrapure water and rinsed with ethanol, dried and then cellulose and cellulose reserve; metatitanic acid, polyethylene glycol and water in 70 90 DEG C, stirring for 16 24 hours, followed by filtration, ultra pure water and ethanol washing and drying to obtain the metatitanic acid modified cellulose. The modified cellulose modified by the present invention can adsorb and remove two lead from the water body.
【技术实现步骤摘要】
一种偏钛酸改性纤维素及其制备方法
本专利技术属于材料领域，具体涉及一种偏钛酸改性纤维素及其制备方法。
技术介绍
纤维素是一种广泛存在、可生物降解并可再生的资源。纤维素是由许多β-D-葡萄糖分子脱水缩合而形成，表面含大量活性官能集团如羟基、羧基等。纤维素的这一结构特点使其可以经过一系列的化学改性而制取各种高分子功能材料。改性纤维素吸附剂就是其中重要发展方向之一。这类吸附剂具有吸附容量大、稳定性高、可再生等优点。
技术实现思路
本专利技术的目的是提供一种偏钛酸改性纤维素及其制备方法。上述目的是通过如下技术方案实现的：一种偏钛酸改性纤维素，由如下方法制备而成：取树皮经清洗、烘干和粉碎后添加到正己烷中加热搅拌脱蜡，过滤、洗净并烘干；将脱蜡产物与氢氧化钠溶液在常温条件搅拌反应，过滤，依次用超纯水和乙醇冲洗，烘干得纤维素备用；然后将纤维素与偏钛酸、聚乙二醇和水于70-90℃搅拌反应16-24小时，过滤，依次用超纯水和乙醇冲洗，烘干即得。进一步地，制备纤维素时，1g树皮对应添加正己烷15-25mL。进一步地，所述氢氧化钠溶液的摩尔浓度为3-5mol/L。进一步地，脱蜡产物与氢氧化钠...
【技术保护点】
一种偏钛酸改性纤维素，其特征在于，由如下方法制备而成：取树皮经清洗、烘干和粉碎后添加到正己烷中加热搅拌脱蜡，过滤、洗净并烘干；将脱蜡产物与氢氧化钠溶液在常温条件搅拌反应，过滤，依次用超纯水和乙醇冲洗，烘干得纤维素备用；然后将纤维素与偏钛酸、聚乙二醇和水于70‑90℃搅拌反应16‑24小时，过滤，依次用超纯水和乙醇冲洗，烘干即得所述偏钛酸改性纤维素。
【技术特征摘要】
1.一种偏钛酸改性纤维素，其特征在于，由如下方法制备而成：取树皮经清洗、烘干和粉碎后添加到正己烷中加热搅拌脱蜡，过滤、洗净并烘干；将脱蜡产物与氢氧化钠溶液在常温条件搅拌反应，过滤，依次用超纯水和乙醇冲洗，烘干得纤维素备用；然后将纤维素与偏钛酸、聚乙二醇和水于70-90℃搅拌反应16-24小时，过滤，依次用超纯水和乙醇冲洗，烘干即得所述偏钛酸改性纤维素。2.根据权利要求1所述的偏钛酸改性纤维素，其特征在于：制备纤维素时，1g树皮对应添加正己烷15-25mL。3.根据权利要...
【专利技术属性】
技术研发人员：韦荣群，
申请(专利权)人：启东祥瑞建设有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。