The present invention relates to the technical field of modified rubber, in particular relates to a modified three EPDM rubber and its preparation method, the modified three EPDM comprises the following raw materials in weight portion: three 40 EPDM 80 copies, 60 copies, 20 silicone rubber reinforcing agent 50, 30 coupling agent 8 12 copies, 8 copies, 4 compatibilizer filler 1 5 copies, 2.5 copies, 1.5 curing agent lubricant 2 1. Three modified EPDM has high mechanical strength prepared by the invention, high and low temperature resistance, ozone resistance, weathering and excellent flame retardant properties and electrical insulation properties, also has good oil resistance, steam resistance, water resistance and corrosion resistance.
【技术实现步骤摘要】
一种改性三元乙丙橡胶及其制备方法
本专利技术涉及改性橡胶
，具体涉及一种改性三元乙丙橡胶及其制备方法。
技术介绍
三元乙丙橡胶不仅具有优异的耐热、耐氧、耐臭氧、耐候以及耐老化性能，而且具有良好的耐化学品、电绝缘性能、低温性能，此外，其还具有低密度、高填充性和耐热水性等，目前已广泛应用于电线电缆、汽车部件、耐热胶管、家电等领域，但是三元乙丙橡胶也存在着耐油性差、硫化速度慢的缺点，另外，其作为有机高分子材料，存在易燃烧的缺陷。随着世界工业的迅猛发展，对三元乙丙橡胶的数量和质量上的要求越来越高。单纯的三元乙丙橡胶材料已不能完全满足要求，其制品在使用的过程中往往存在耐油性不足、阻燃性欠佳、耐热性和耐老化性不理想的缺陷，需要对其进行改性。
技术实现思路
为了克服现有技术中存在的缺点和不足，本专利技术的目的在于提供一种改性三元乙丙橡胶，该改性三元乙丙橡胶具有较高的机械强度，耐高低温、耐气候老化、耐臭氧以及优良的阻燃性能和电气绝缘性能，还具有较好的耐油性、耐蒸汽性、耐热水性和耐酸碱性能。本专利技术的另一目的在于提供一种改性三元乙丙橡胶的制备方法，该制备方法步骤简单，操作控制方...
【技术保护点】
一种改性三元乙丙橡胶，其特征在于：所述改性三元乙丙橡胶包括如下重量份的原料：
【技术特征摘要】
1.一种改性三元乙丙橡胶，其特征在于：所述改性三元乙丙橡胶包括如下重量份的原料：2.根据权利要求1所述的一种改性三元乙丙橡胶，其特征在于：所述三元乙丙橡胶是由乙烯/丙烯/乙叉降冰片烯共聚物、乙烯/丙烯/双环戊二烯共聚物和乙烯/丙烯/1，4-己二烯共聚物以重量比2-4:1.5-2.5:1组成的混合物。3.根据权利要求1所述的一种改性三元乙丙橡胶，其特征在于：所述硅橡胶是由甲基乙烯基硅橡胶A、甲基乙烯基硅橡胶B和甲基乙烯基硅橡胶C以重量比4-8：1-3：1组成的混合物；其中，甲基乙烯基硅橡胶A的乙烯基含量为0.1-0.2％，分子量为66-68万；甲基乙烯基硅橡胶B的乙烯基含量为0.2-0.4％，分子量为64-66万；甲基乙烯基硅橡胶C的乙烯基含量为5.8-6.8％，分子量为62-64万。4.根据权利要求1所述的一种改性三元乙丙橡胶，其特征在于：所述补强剂是由不饱和羧酸盐、氧化钙晶须和白炭黑以重量比0.8-1.2:1:1.5-2.5组成的混合物，其中，所述白炭黑为粒径在10-50nm、比表面积在200-300m2/g的气相白炭黑。5.根据权利要求1所述的一种改性三元乙丙橡胶，其特征在于：所述偶联剂是由γ―氨丙基三乙氧基硅烷、二甲基二乙氧基硅烷和乙烯基三甲氧基硅烷以重量比1.5-2.5:0.8-1.2:1组成的混合物。...
【专利技术属性】
技术研发人员：尹川，
申请(专利权)人：广州市鑫橡极科技有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。