For indoor decoration, building a kaolin coating preparation method, and relates to a preparation method of architectural coatings, the kaolin mine after 6 months of natural weathering into grains and dried in a kiln, firing 5 7 hours, firing temperature is 700 degrees Celsius to 1200, burning kaolin prepared cooked material the broken screen, divided into 80 mesh 325 mesh ranging from 73.2% to 22% 4%N2098 (kaolin, calcium powder, powder), 0.8%CH (40 cellulose), mixing into powder coating; when used with 75% evenly, can for the interior decoration of kaolin coating; 1 tons of kaolin powder against 80 kg can be cooked latex powder mixing evenly, namely the interior decoration coating kaolin. The kaolin paint of the invention has obvious comprehensive effect, in particular to purify air, remove formaldehyde, eliminate peculiar smell, sterilize and disinfect, and is favorable for regulating the microcirculation of human body. The preparation process is scientific and reasonable and the conditions are favorable.
【技术实现步骤摘要】
一种建筑用室内装饰高岭土涂料制备方法
本专利技术涉及一种建筑涂料制备方法，特别是涉及一种建筑用室内装饰高岭土涂料制备方法。
技术介绍
现有室内涂料在吸附和净化空气以及释放有益分子等方面欠缺、达不到对人体有益的完美纯绿色环保的室内装饰涂料效果。
技术实现思路
本专利技术的目的在于提供一种建筑用室内装饰高岭土涂料制备方法，本专利技术高岭土涂料综合效果明显，特别是可净化空气、清除甲醛、消除异味、杀菌消毒，利于调节人体微循环，其制备工艺科学合理、条件优越。本专利技术的目的是通过以下技术方案实现的：一种建筑用室内装饰高岭土涂料制备方法，所述涂料的制备方法包括以下制备高岭土熟粉过程：首先把高岭土矿经过6个月自然风化成颗粒状，晒干后进入窑内，进行5-7小时的烧制，烧制温度为700-1200摄氏度，对烧制好的熟高岭土料进行破碎过筛，分成80目-325目不等，按73.2%高岭土，22%灰钙粉，4%N2098（胶粉）,0.8%CH-40（纤维素），均匀混料成粉状涂料。使用时加水75%搅拌均匀，即可为室内装饰高岭土涂料。本专利技术的优点与效果是：1.本专利技术高岭土涂料可净化空气、清除甲醛...
【技术保护点】
一种建筑用室内装饰高岭土涂料制备方法，其特征在于，所述涂料的制备方法包括以下制备高岭土熟粉过程：首先把高岭土矿经过6个月自然风化成颗粒状，晒干后进入窑内，进行5‑7小时的烧制，烧制温度为700‑1200摄氏度，对烧制好的熟高岭土料进行破碎过筛，分成80目‑325目不等，按73.2%高岭土，22%灰钙粉，4%N2098（胶粉）,0.8%CH‑40（纤维素），均匀混料成粉状涂料；使用时加水75%搅拌均匀，即可为室内装饰高岭土涂料；1吨高岭土熟粉兑80公斤可再分散性乳胶粉比例搅拌均匀，即为本室内装饰高岭土涂料。
【技术特征摘要】
1.一种建筑用室内装饰高岭土涂料制备方法，其特征在于，所述涂料的制备方法包括以下制备高岭土熟粉过程：首先把高岭土矿经过6个月自然风化成颗粒状，晒干后进入窑内，进行5-7小时的烧制，烧制温度为700-1200摄氏度，对烧制好的熟高岭土料进行破碎过筛，分成80...