The invention relates to a preparation method of kaolin for glass fiber. Method for preparing kaolin used by glass fiber, characterized in that it comprises the following steps: 1) the original kaolin powder at 600 to 650 DEG C pre calcined 2 ~ 2.5h, to get the pre calcined kaolin; the kaolin raw powder particle size less than 325 mesh; 2) additives to the pre calcined kaolin with adding additives. ZnO and CeO: 2, ZnO content is the quality of pre calcined kaolin 1 per thousand to 5 per thousand, CeO: 2 adding quality of pre calcined kaolin 1 per thousand to 5 per thousand; mixing with glass fiber was prepared from kaolin; glass fiber with kaolin adsorption water content H down, 2, O = = 2% -. The invention eliminates the domestic kaolin as filler used in glass fiber industry which occur when bubbles, coloring and melt phenomenon, and more conducive to the homogenization of glass fiber and the stability of product quality; products meet national standards and industry standards, can replace the imported kaolin used by glass, while reducing the production cost of the glass fiber.
【技术实现步骤摘要】
本专利技术涉及一种玻璃纤维用高岭土的制备方法。
技术介绍
玻璃纤维是无机非金属材料中的新型功能材料和结构材料,广泛应用于电子、通信、核 能、航空、航天、兵器、舰艇及海洋开发、遗传工程等高新科技产业，成为我国21世纪不可 缺少的可持续发展的高新技术材料。传统玻纤配方中一般添加叶蜡石，其理论化学式为A1203 '4Si02 但近年来叶蜡石(地 开石)开采过量，逐渐贫化，杂质多，质量不稳定，中国国内还没有上规模的叶蜡石选矿加工企 业。国外有关资料报道，欧美国家和台湾地区的玻纤企业,采用精选或质地好的高岭土取代叶 蜡石作玻纤原料，生产高强度和电子级玻纤，产品质量好。高岭土主要由高岭石、多水高岭石、三水铝石、长石和石英组成。我国玻纤用高岭土主 要从美国进口，美国高岭土纯度高、质量稳定，但运输成本较高。我国高岭土和美国玻纤用 高岭土相比杂质含量和化学需氧量(C0D)均高，在玻纤生产过程中易导致断丝、气泡和致 色等现象，制约了我国高岭土在玻纤行业中的应用。针对我国高岭土的特点制备玻纤用高岭 土取代进口高岭土具有重要意义。
技术实现思路
本专利技术的目的在于提供一种，该方法制备的玻...
【技术保护点】
玻纤用高岭土的制备方法，其特征在于它包括如下步骤： １）将高岭土原矿粉料在６００～６５０℃预煅烧２．０～２．５ｈ，得预煅烧高岭土；所述高岭土原矿粉料的粒径小于３２５目； ２）向预煅烧高岭土中外加添加剂，添加剂为ＺｎＯ和ＣｅＯ↓［２］，ＺｎＯ加入量为预煅烧高岭土质量的１‰～５‰，ＣｅＯ↓［２］加入量为预煅烧高岭土质量的１‰～５‰；混合搅拌，得玻纤用高岭土；制备得到的玻纤用高岭土吸附水含量Ｈ↓［２］Ｏ↑［－］≤２．００％。
【技术特征摘要】
【专利技术属性】
技术研发人员：肖国琪，严春杰，韩利雄，李予晋，海书杰，
申请(专利权)人：中国地质大学武汉，云南天鸿高岭矿业有限公司，
类型：发明
国别省市：83[中国|武汉]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。